PA612 612GF33 HE A SCHULMAN USA
SCHULAMID®
--
Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | A SCHULMAN USA/612GF33 HE |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 80 kJ/m² |
| -30°C | ISO 179/1eU | 65 kJ/m² |
| Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/612GF33 HE |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 10500 Mpa | |
| Flexural modulus | ISO 178 | 10000 Mpa | |
| bending strength | 3.7% 应变 | ISO 178 | 280 Mpa |
| 3.5% 应变 | ISO 178 | 280 Mpa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 175 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 3.2 % |
| physical property | Test Condition | Test Method | A SCHULMAN USA/612GF33 HE |
|---|---|---|---|
| viscosity number | H2SO4（硫酸） | ISO 307 | 125 cm³/g |
| Thermal performance | Test Condition | Test Method | A SCHULMAN USA/612GF33 HE |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/Bf | 215 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/Af | 195 °C |
| injection | Test Condition | Test Method | A SCHULMAN USA/612GF33 HE |
|---|---|---|---|
| drying time | 3.0 to 6.0 hr | ||
| Suggested maximum material return ratio | 20 % | ||
| Suggested maximum moisture content | 0.040 to 0.10 % | ||
| Processing (melt) temperature | 240 to 280 °C | ||
| drying temperature | 80 °C | ||
| Temperature | 50 to 90 °C |