PA66 Zytel® 70G30REF NC010 DUPONT USA
175
- Unit Price:US$ 2,761 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:21.3MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜Hydrolysis resistance
- Application Areas:Automotive sector｜Electrical appliances
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 1.1 % | |
| ISO 294-4 | 0.30 % | ||
| Water absorption rate | ISO 62 | 6.9 % | |
| ISO 62 | 2.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | ISO 3795 | 24 mm/min | |
| UL flame retardant rating | UL 94 | HB | |
| UL 94 | HB | ||
| Limiting Oxygen Index | ISO 4589-2 | 24 % | |
| FMVSS combustion rate | FMVSS 302 | SE/B | |
| atomization | ISO 6452 | 95 % | |
| ISO 6452 | 3.0E-4 g |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 9800 Mpa | |
| tensile strength | ISO 527-2 | 195 Mpa | |
| Tensile strain | ISO 527-2 | 3.5 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 60 kJ/m² | |
| ISO 179/1eU | 80 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt density | 1.21 g/cm³ | ||
| Specific Heat Capacity of Melt | 2290 J/kg/°C | ||
| Thermal Conductivity of Melt | 0.21 W/m/K | ||
| Emission of Organic Compounds | VDA 277 | 6.00 µgC/g | |
| Odor | VDA 270 | 4.50 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 62631-3-2 | -- ohms | |
| Volume resistivity | IEC 62631-3-1 | 1.0E+11 ohms·m | |
| Dissipation Factor | IEC 62631-2-1 | 0.016 | |
| IEC 62631-2-1 | 0.016 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 0 | |
| IEC 60112 | PLC 0 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.20 % | ||
| Processing (melt) temperature | 285 to 305 °C | ||
| Melt Temperature, Optimum | 295 °C | ||
| Temperature | 70 to 120 °C | ||
| Mold Temperature, Optimum | 100 °C | ||
| pressure holding | 50.0 to 100 Mpa | ||
| yes | |||
| Hold Pressure Time | 3.00 s/mm | ||
| Maximum Screw Tangential Speed | 12 m/min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 260 °C | |
| ISO 75-2/A | 253 °C | ||
| Glass Transition Temperature | ISO 11357-2 | 80.0 °C | |
| melting temperature | ISO 11357-3 | 262 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 2.8E-5 cm/cm/°C | |
| ISO 11359-2 | 9.5E-5 cm/cm/°C | ||
| Effective thermal diffusivity coefficient | 6.85E-8 m²/s |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.