PA66 70G30REF NC010 DUPONT USA
Zytel®
Automotive sector、Electrical appliances
Thermal stability、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/70G30REF NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 80 kJ/m² |
| -30°C | ISO 179/1eU | 60 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/70G30REF NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 9800 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.5 % |
| tensile strength | 断裂 | ISO 527-2 | 195 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/70G30REF NC010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 3.00 mm | UL 746 | PLC 0 |
| IEC 60112 | PLC 0 | ||
| Dissipation Factor | 100 Hz | IEC 62631-2-1 | 0.016 |
| 1 MHz | IEC 62631-2-1 | 0.016 | |
| Volume resistivity | IEC 62631-3-1 | 1.0E+11 ohms·m | |
| Surface Resistivity | IEC 62631-3-2 | -- ohms |
| flammability | Test Condition | Test Method | DUPONT USA/70G30REF NC010 |
|---|---|---|---|
| atomization | F-value (refraction) | ISO 6452 | 95 % |
| UL flame retardant rating | UL 94 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 24 % | |
| atomization | G-value (condensate) | ISO 6452 | 3.0E-4 g |
| FMVSS combustion rate | FMVSS 302 | SE/B | |
| burning rate | 1.00 mm | ISO 3795 | 24 mm/min |
| Filling analysis | Test Condition | Test Method | DUPONT USA/70G30REF NC010 |
|---|---|---|---|
| Odor | VDA 270 | 4.50 | |
| Thermal Conductivity of Melt | 0.21 W/m/K | ||
| Melt density | 1.21 g/cm³ | ||
| Emission of Organic Compounds | VDA 277 | 6.00 µgC/g | |
| Specific Heat Capacity of Melt | 2290 J/kg/°C |
| physical property | Test Condition | Test Method | DUPONT USA/70G30REF NC010 |
|---|---|---|---|
| Water absorption rate | 饱和, 23°C, 2.00 mm | ISO 62 | 6.9 % |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.0 % | |
| Shrinkage rate | 流量 | ISO 294-4 | 0.30 % |
| 横向流量 | ISO 294-4 | 1.1 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/70G30REF NC010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 262 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 260 °C |
| Effective thermal diffusivity coefficient | 6.85E-8 m²/s | ||
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 253 °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 2.8E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 9.5E-5 cm/cm/°C | |
| Glass Transition Temperature | ISO 11357-2 | 80.0 °C |
| injection | Test Condition | Test Method | DUPONT USA/70G30REF NC010 |
|---|---|---|---|
| pressure holding | 50.0 to 100 Mpa | ||
| Maximum Screw Tangential Speed | 12 m/min | ||
| pressure holding | Drying Recommended | yes | |
| Suggested maximum moisture content | 0.20 % | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Processing (melt) temperature | 285 to 305 °C | ||
| drying temperature | 80 °C | ||
| Temperature | 70 to 120 °C | ||
| Melt Temperature, Optimum | 295 °C | ||
| Hold Pressure Time | 3.00 s/mm | ||
| Mold Temperature, Optimum | 100 °C |