Material Description

Material Properties:Low water absorption｜Rigidity and strength
Application Areas:Electronic and Electrical Applications｜Automotive components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	65 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	65 kJ/m²

flammability	Test Condition	Test Method	Test Result
Extreme Oxygen Index		ISO 4589-2	50 %
Polymer Abbreviation			PA6T/6-GF30 FR
Hot filament ignition temperature	0.40 mm	IEC 60695-2-13	775 °C
Burning wire flammability index	0.40 mm	IEC 60695-2-12	960 °C

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	240 Mpa
Bending modulus		ISO 178	11000 Mpa
Tensile strain	Break	ISO 527-2	2.5 %
tensile strength	Break	ISO 527-2	150 Mpa
Tensile modulus		ISO 527-2	11000 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			110 °C
drying time			8.0 hr
Suggested maximum moisture content			0.030 %
Hopper temperature			80 °C
Temperature at the rear of the barrel			300 °C
Temperature in the middle of the barrel			310 °C
Temperature at the front of the material cylinder			320 °C
Spray nozzle temperature			320 °C
Processing (melt) temperature			310 to 330 °C
Mold temperature			80 to 120 °C
Residence Time			< 5.0 min
Screw speed			< 18 m/min

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ISO 11357-3	290 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	220 °C

Physical properties	Test Condition	Test Method	Test Result
Mold Shrinkage - Model Heating	1.50 mm		0.10 %
Stickiness	96% H2SO4	ISO 307	120 cm³/g
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.4 to 1.8 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	4.3 to 5.3 %
Shrinkage rate	Flow	ISO 294-4	0.30 %
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.70 %
Melt Volume Flow Rate (MVR)	325°C/5.0 kg	ISO 1133	45.0 cm3/10min
Apparent density			0.70 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	Solution A	IEC 60112	V
Dissipation factor	1 MHz	IEC 60250	0.015
Relative permittivity	1 MHz	IEC 60250	3.90
Volume resistivity		IEC 60093	1.0E+17 ohms·cm
Surface resistivity		IEC 60093	-- ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.