PA610 LNP™ THERMOCOMP™ QCL-4036 BK SABIC INNOVATIVE US

338

Unit Price:US$ 4,780 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Conductive｜Glass fiber reinforced
Application Areas:Electronic and Electrical Applications｜Fitness equipment
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	10 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	53 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	10.0 J
Multi axis Instrumented Impact Energy		ISO 6603-2	3.58 J

mechanical properties	Test Condition	Test Method	Test Result
Wear factor	Washer	ASTM D3702Modified	26.0 10^-10in^5-min/ft-lb-hr
Tensile modulus		ASTM D638	16600 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	15600 Mpa
tensile strength	Break	ASTM D638	201 Mpa
tensile strength	tensile strength	Break	ISO 527-2/5	197 Mpa
elongation	Break	ASTM D638	2.7 %
Tensile strain	Break	ISO 527-2/5	2.7 %
Bending modulus	50.0mmSpan	ASTM D790	12400 Mpa
Bending modulus	Bending modulus		ISO 178	12500 Mpa
bending strength		ISO 178	280 Mpa
	bending strength	Yield,50.0mmSpan	ASTM D790	289 Mpa
	bending strength	bending strength	Break,50.0mmSpan	ASTM D790	288 Mpa
Friction coefficient	Dynamic	ASTM D3702Modified	0.39
Friction coefficient	Friction coefficient	Static	ASTM D3702Modified	0.33
Wear factor	Ring	ASTM D3702Modified	0.300 10^-10in^5-min/ft-lb-hr

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	221 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	212 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	206 °C
Linear coefficient of thermal expansion	MD：-30to30°C	ASTM D696	2.1E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-30to30°C	ASTM D696	5.8E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：24hr	ASTM D955	0.060-0.080 %
Shrinkage rate	Shrinkage rate	TD：24hr	ASTM D955	0.40-0.60 %
Water absorption rate	24hr,50%RH	ASTM D570	0.19 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.30 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA610 LNP™ THERMOCOMP™ QCL-4036 BK SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet