PC INFINO® HF-1023IM Samsung Cheil South Korea

301

Unit Price:US$ 3,240 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜High mobility｜ Impact resistance｜High liquidity
Application Areas:Electrical field｜Electronic field｜Daily products
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	68	kJ/m²
Impact strength of cantilever beam gap	23°C, 3.18 mm	ASTM D256	690	J/m
	Impact strength of cantilever beam gap	23°C, 6.35 mm	ASTM D256	540	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C6	ISO 180/1A	63	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--3	ASTM D638	1900	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/50	2100	Mpa
tensile strength	Yield3	ASTM D638	59.0	Mpa
	tensile strength	Yield	ISO 527-2/50	60.0	Mpa
		tensile strength	Break3	ASTM D638	69.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	96.0	Mpa
elongation	Break3	ASTM D638	120	%
elongation	elongation	Break	ISO 527-2/50	100	%
Bending modulus	--4	ASTM D790	2000	Mpa
Bending modulus	Bending modulus	--5	ISO 178	2100	Mpa
bending strength	--4	ASTM D790	83.0	Mpa
bending strength	bending strength	--5	ISO 178	88.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Hot air dryer			100	°C
Vacuum drying machine			100	°C
Hot air dryer			2.0 to 4.0	hr
Vacuum drying machine			4.0 to 6.0	hr
Suggested maximum moisture content			< 0.020	%
Temperature at the rear of the barrel			270	°C
Temperature in the middle of the barrel			280	°C
Temperature at the front of the material cylinder			290	°C
Spray nozzle temperature			300	°C
Mold temperature			80 to 100	°C
Injection pressure			98.1	Mpa
Back pressure			0.981 to 2.94	Mpa
Screw speed			40 to 80	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm	ISO 75-2/B	133	°C
	Hot deformation temperature	0.45 MPa, Annealed, 4.00 mm	ISO 75-2/B	130	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	126	°C
			Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm	ISO 75-2/A	120	°C
			Hot deformation temperature	Hot deformation temperature	1.8 MPa, Annealed, 4.00 mm	ISO 75-2/A	120	°C
Vicat softening temperature	--	ISO 306/B50	140	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	142	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	本色	ASTM D792	1.18	g/cm³
melt mass-flow rate	250°C/10.0 kg	ASTM D1238	22	g/10 min
Shrinkage rate	Flow : 3.20 mm	ASTM D955	0.44 - 0.53	%
	Shrinkage rate	Across FlowFlow : 3.20 mm	ASTM D955	0.45 - 0.55	%
		Shrinkage rate	横向Flow : 2.00 mm	ISO 294-4	0.45 - 0.55	%
		Shrinkage rate	Shrinkage rate	Flow : 2.00 mm	ISO 294-4	0.44 - 0.53	%
Water absorption rate	Saturation, 23°C	ASTM D570	0.35	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	120
Rockwell hardness	Rockwell hardness	R -Sale	ISO 2039-2	120

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC INFINO® HF-1023IM Samsung Cheil South Korea

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index