Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HF-1023IM Samsung Cheil South Korea
INFINO®
Electrical field、Electronic field、Daily products
High impact resistance、High mobility、 Impact resistance、High liquidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/HF-1023IM |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 68 kJ/m² |
| Impact strength of cantilever beam gap | 23°C, 3.18 mm | ASTM D256 | 690 J/m |
| 23°C6 | ISO 180/1A | 63 kJ/m² | |
| 23°C, 6.35 mm | ASTM D256 | 540 J/m |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/HF-1023IM |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 120 |
| R 级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/HF-1023IM |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 Mpa |
| 屈服3 | ASTM D638 | 59.0 Mpa | |
| elongation | 断裂3 | ASTM D638 | 120 % |
| bending strength | --4 | ASTM D790 | 83.0 Mpa |
| --5 | ISO 178 | 88.0 Mpa | |
| Tensile modulus | --3 | ASTM D638 | 1900 Mpa |
| -- | ISO 527-2/50 | 2100 Mpa | |
| elongation | 断裂 | ISO 527-2/50 | 100 % |
| Flexural modulus | --4 | ASTM D790 | 2000 Mpa |
| --5 | ISO 178 | 2100 Mpa | |
| tensile strength | 断裂3 | ASTM D638 | 69.0 Mpa |
| 断裂 | ISO 527-2/50 | 96.0 Mpa |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/HF-1023IM |
|---|---|---|---|
| density | 本色 | ASTM D792 | 1.18 g/cm³ |
| Shrinkage rate | 横向流动 : 3.20 mm | ASTM D955 | 0.45 - 0.55 % |
| 流量 : 2.00 mm | ISO 294-4 | 0.44 - 0.53 % | |
| 流动 : 3.20 mm | ASTM D955 | 0.44 - 0.53 % | |
| 横向流量 : 2.00 mm | ISO 294-4 | 0.45 - 0.55 % | |
| Water absorption rate | 饱和, 23°C | ASTM D570 | 0.35 % |
| melt mass-flow rate | 250°C/10.0 kg | ASTM D1238 | 22 g/10 min |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/HF-1023IM |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 142 °C |
| Heat distortion temperature | 0.45 MPa, 退火, 4.00 mm，HDT | ISO 75-2/B | 130 °C |
| vicat | -- | ISO 306/B50 | 140 °C |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm，HDT | ISO 75-2/A | 120 °C |
| 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 126 °C | |
| 0.45 MPa, 未退火, 4.00 mm，HDT | ISO 75-2/B | 133 °C | |
| 1.8 MPa, 退火, 4.00 mm，HDT | ISO 75-2/A | 120 °C |
| injection | Test Condition | Test Method | Samsung Cheil South Korea/HF-1023IM |
|---|---|---|---|
| screw speed | 40 to 80 rpm | ||
| Suggested maximum moisture content | < 0.020 % | ||
| Vacuum dryer | 100 °C | ||
| Injection Pressure | 98.1 Mpa | ||
| Hot air dryer | 2.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 280 °C | ||
| Temperature at the rear of the barrel | 270 °C | ||
| Vacuum dryer | 4.0 to 6.0 hr | ||
| Temperature at the front of the material cylinder | 290 °C | ||
| Back pressure | 0.981 to 2.94 Mpa | ||
| Temperature | 80 to 100 °C | ||
| Hot air dryer | 100 °C | ||
| Spray nozzle temperature | 300 °C |