'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPS FORTRON® 1140L6 BK CELANESE USA
473
- Unit Price:US$ 7,160 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:41MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced｜High temperature resistance
- Application Areas:fibre｜Bottle cap
- Color:--
- Grade:Injection grade
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 | kJ/m² |
| -30°C | ISO 179/1eA | 10 | kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 53 | kJ/m² |
| -30°C | ISO 179/1eU | 53 | kJ/m² | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 34 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 | kJ/m² |
| 23°C | ISO 180/1A | 10 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.38mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-0 | ||
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | ISO 62 | 0.02 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile strain | Break | ISO 527-2/1A/5 | 1.9 | % |
| elongation | Break,23°C | ASTM D638 | 2.0 | % |
| tensile strength | Break | ISO 527-2/1A/5 | 195 | Mpa |
| Break,23°C | ASTM D638 | 200 | Mpa | |
| bending strength | ISO 178 | 285 | Mpa | |
| Bending modulus | 23°C | ISO 178 | 14500 | Mpa |
| ISO 178 | 14500 | Mpa | ||
| elongation | Break | ISO 527-1 | 1.9 | % |
| tensile strength | ISO 527-1 | 195 | Mpa | |
| Tensile modulus | ISO 527-1 | 14700 | Mpa | |
| Rockwell hardness | ISO 2039-2 | 100 | M-scale | |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 10 | kJ/m² |
| bending strength | ISO 178 | 285 | Mpa | |
| Tensile modulus | ISO 527-2/1A/1 | 14700 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.6E-05 | cm/cm/°C |
| Melting temperature | ISO 11357-3 | 280 | °C | |
| UL flame retardant rating | UL 94 | V-0 | ||
| Hot deformation temperature | 1.80Mpa | ISO 75-1 | 270 | °C |
| 1.8MPa,Unannealed | ASTM D648 | 265 | °C | |
| 1.8MPa,Unannealed | ISO 75-2/A | 270 | °C | |
| 8.0MPa,Unannealed | ISO 75-2/C | 215 | °C | |
| Glass transition temperature | ISO 11357-2 | 90.0 | °C | |
| Hot deformation temperature | 0.45MPa,Annealed | ASTM D648 | 280 | °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 4.2E-05 | cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | ISO 2577 | 0.2-0.6 | % | |
| density | ISO 1183 | 1.65 | g/cm³ | |
| SpecificHeatCapacity of Melt | Internal Method | 1500 | J/kg/°C | |
| Specific volume | ASTM D792 | 0.625 | cm³/g | |
| density | ISO 1183 | 1.65 | g/cm³ | |
| ASTM D792 | 1.60 | g/cm³ | ||
| Shrinkage rate | TD | ISO 294-4 | 0.40-0.60 | % |
| MD | ISO 294-4 | 0.20-0.60 | % | |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.020 | % |
| Spiral flow length | Internal Method | 21.5 | ||
| melt mass-flow rate | ASTM D1238 | 19 | g/10min | |
| Shrinkage rate | MD | ASTM D955 | 0.20-0.30 | % |
| TD | ASTM D955 | 0.50-0.70 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dissipation factor | 1MHz | IEC 60250 | 2E-03 | |
| 1MHz | ASTM D150 | 1E-03 | ||
| Arc resistance | ASTM D495 | 134 | sec | |
| Relative permittivity | 1MHz | IEC 60250 | 4.10 | |
| Dissipation factor | 1kHz | ASTM D150 | 1E-03 | |
| Dielectric constant | 1MHz | ASTM D150 | 3.50 | |
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| Volume resistivity | ASTM D257 | 1E+16 | ohms·cm | |
| IEC 60093 | >1.0E+15 | ohms·cm | ||
| Dielectric strength | ASTM D149 | 15 | KV/mm | |
| IEC 60243-1 | 28 | KV/mm | ||
| Dielectric constant | 1kHz | ASTM D150 | 3.50 | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M-Scale | ASTM D785 | 100 | |
| M-Scale | ISO 2039-2 | 100 | ||
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| CSARating | 8.40E-7mm | CSAF-1 | A00 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.