Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS 1140L6 BK CELANESE USA
FORTRON®
fibre、Bottle cap
Flame retardant、Glass fiber reinforced、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/1140L6 BK |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 34 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 53 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 10 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 53 kJ/m² |
| Supplementary Information | Test Condition | Test Method | CELANESE USA/1140L6 BK |
|---|---|---|---|
| CSARating | 8.40E-7mm | CSAF-1 | A00 |
| hardness | Test Condition | Test Method | CELANESE USA/1140L6 BK |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 100 |
| M级 | ISO 2039-2 | 100 |
| Basic performance | Test Condition | Test Method | CELANESE USA/1140L6 BK |
|---|---|---|---|
| Water absorption rate | ISO 62 | 0.02 % |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/1140L6 BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 14700 Mpa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 195 Mpa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 10 kJ/m² |
| Rockwell hardness | ISO 2039-2 | 100 M-scale | |
| tensile strength | 断裂,23°C | ASTM D638 | 200 Mpa |
| ISO 527-1 | 195 Mpa | ||
| bending strength | ISO 178 | 285 Mpa | |
| Flexural modulus | ISO 178 | 14500 Mpa | |
| 23°C | ISO 178 | 14500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.9 % |
| Tensile modulus | ISO 527-1 | 14700 Mpa | |
| elongation | 断裂 | ISO 527-1 | 1.9 % |
| 断裂,23°C | ASTM D638 | 2.0 % |
| Electrical performance | Test Condition | Test Method | CELANESE USA/1140L6 BK |
|---|---|---|---|
| Dissipation Factor | 1kHz | ASTM D150 | 1E-03 |
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| Dissipation Factor | 1MHz | ASTM D150 | 1E-03 |
| dielectric constant | 1kHz | ASTM D150 | 3.50 |
| 1MHz | ASTM D150 | 3.50 | |
| relative permittivity | 1MHz | IEC 60250 | 4.10 |
| Dissipation Factor | 1MHz | IEC 60250 | 2E-03 |
| arc resistance | ASTM D495 | 134 sec | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| dielectric strength | IEC 60243-1 | 28 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 15 KV/mm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| flammability | Test Condition | Test Method | CELANESE USA/1140L6 BK |
|---|---|---|---|
| UL flame retardant rating | 0.38mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | CELANESE USA/1140L6 BK |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 0.2-0.6 % | |
| SpecificHeatCapacity of Melt | 内部方法 | 1500 J/kg/°C | |
| Shrinkage rate | TD | ISO 294-4 | 0.40-0.60 % |
| MD | ASTM D955 | 0.20-0.30 % | |
| MD | ISO 294-4 | 0.20-0.60 % | |
| spiral flow length | 内部方法 | 21.5 | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.020 % |
| density | ASTM D792 | 1.60 g/cm³ | |
| Shrinkage rate | TD | ASTM D955 | 0.50-0.70 % |
| Specific volume | ASTM D792 | 0.625 cm³/g | |
| density | ISO 1183 | 1.65 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 19 g/10min |
| Thermal performance | Test Condition | Test Method | CELANESE USA/1140L6 BK |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 280 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 265 °C |
| 1.80Mpa，HDT | ISO 75-1 | 270 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 270 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.6E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ASTM D648 | 280 °C |
| 8.0MPa,未退火，HDT | ISO 75-2/C | 215 °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 4.2E-05 cm/cm/°C |
| UL flame retardant rating | UL 94 | V-0 | |
| Glass Transition Temperature | ISO 11357-2 | 90.0 °C |