PP ExxonMobil™  AP3AW EXXONMOBIL SINGAPORE

333
  • Unit Price:US$ 1,552 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    53.5MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Low warpageHigh rigidityHigh impact resistanceMiddle flowLight resistance
  • Application Areas:Battery boxEngine hood partsAutomotive sectorApplication in the automotive fieldParts under the hood of a car
  • Color:--
  • Grade:Injection grade

Material Certification

UL
TDS

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Dart impact-29°C,3.18mmASTM D542018.1 J
Impact strength of cantilever beam gap23°CISO 180/1A8.8 kJ/m²
Impact strength of cantilever beam gap-18°CISO 180/1A4.5 kJ/m²
Impact strength of cantilever beam gap-40°CISO 180/1A3.4 kJ/m²
Impact strength of cantilever beam gap23°CASTM D256A90 J/m
Impact strength of cantilever beam gap-18°CASTM D256A35 J/m
Charpy Notched Impact Strength23°CISO 179/1eA9.9 kJ/m²
Charpy Notched Impact Strength0°CISO 179/1eA4.9 kJ/m²
Charpy Notched Impact Strength-20°CISO 179/1eA3.9 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA3.3 kJ/m²
mechanical propertiesTest ConditionTest MethodTest Result
Bending modulus--6ISO 1781340 Mpa
Bending modulus1%Secant5ASTM D790B1520 Mpa
Bending modulus1%Secant4ASTM D790A1340 Mpa
elongationYieldISO 527-2/505.7 %
elongationYield3ASTM D6385.6 %
tensile strengthYieldISO 527-2/5025.7 Mpa
tensile strengthYield3ASTM D63827.1 Mpa
Tensile modulusISO 527-2/11500 Mpa
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A53.4 °C
Hot deformation temperature0.45MPa,AnnealedASTM D648116 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/Bf92.5 °C
Hot deformation temperature0.45MPa,UnannealedASTM D64899.4 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate230°C/2.16kgASTM D123810 g/10min
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessASTM D78596
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.