PC LUPOY® 1303-07 LG CHEM KOREA

345

Unit Price:US$ 2,930 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:sheet｜lens｜Electrical appliances｜film
Color:--
Grade:--

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ASTM D542	1.586
transmissivity		ASTM D1003	89.0	%
turbidity		ASTM D1003	0.70to1.5	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
InstrumentedDartImpact	23°C,3.20mm,TotalEnergy	ASTM D3763	90.0	J
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	900	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.50mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
Ignition temperature of heating wire	2.0mm	IEC 60695-2-13	850	°C
Extreme Oxygen Index		ASTM D2863	26	%
Average degree of combustion		ASTM D635	3	CM
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ASTM D638	150	%
elongation	elongation	Yield	ASTM D638	6.0	%
tensile strength	Break	ASTM D638	72.0	Mpa
tensile strength	tensile strength	Yield	ASTM D638	60.0	Mpa
Tensile modulus		ASTM D638	2410	Mpa
Wear resistance	雾度变化	Kg/m	45	%
bending strength		ASTM D790	96.0	Mpa
Bending modulus		ASTM D790	2410	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD：-40to82°C	ASTM D696	6.8E-05	cm/cm/°C
Ball pressure temperature		IEC 60598-1	>125	°C
Vicat softening temperature		ASTM D15255	151	°C
Hot deformation temperature	1.8MPa,Annealed,4.00mm	ASTM D648	142	°C
	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ASTM D648	129	°C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Annealed,4.00mm	ASTM D648	145	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ASTM D570	0.32	%
Water absorption rate	Water absorption rate	23°C,24hr	ASTM D570	0.15	%
Shrinkage rate	MD	ASTM D955	0.50-0.70	%
melt mass-flow rate	300°C/1.2kg	ASTM D1238	7.0	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	60Hz	ASTM D150	3.00
Dissipation factor	60Hz	ASTM D150	1E-03
Dielectric strength		ASTM D149	17	KV/mm
Volume resistivity	23°C	ASTM D257	2E+17	ohms·cm
Compared to the anti leakage trace index	2.00mm	IEC 60112	PLC 2
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale	ASTM D785	118
Rockwell hardness	Rockwell hardness	M-Sale	ASTM D785	74

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC LUPOY® 1303-07 LG CHEM KOREA

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index