Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 1303-07 LG CHEM KOREA
LUPOY®
sheet,lens,Electrical appliances,film
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG CHEM KOREA/1303-07 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 900 J/m |
| InstrumentedDartImpact | 23°C,3.20mm,TotalEnergy | ASTM D3763 | 90.0 J |
| hardness | Test Condition | Test Method | LG CHEM KOREA/1303-07 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 74 |
| R计秤 | ASTM D785 | 118 |
| thermal performance | Test Condition | Test Method | LG CHEM KOREA/1303-07 |
|---|---|---|---|
| Ball pressure temperature | IEC 60598-1 | >125 °C | |
| Linear coefficient of thermal expansion | MD：-40到82°C | ASTM D696 | 6.8E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,4.00mm，HDT | ASTM D648 | 129 °C |
| 1.8MPa,Annealed,4.00mm，HDT | ASTM D648 | 142 °C | |
| 0.45MPa,Annealed,4.00mm，HDT | ASTM D648 | 145 °C | |
| vicat | ASTM D15255 | 151 °C |
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/1303-07 |
|---|---|---|---|
| wear resistance | 雾度变化 | Kg/m | 45 % |
| Tensile modulus | ASTM D638 | 2410 Mpa | |
| elongation | 断裂 | ASTM D638 | 150 % |
| tensile strength | 屈服 | ASTM D638 | 60.0 Mpa |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| flexural modulus | ASTM D790 | 2410 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 72.0 Mpa |
| bending strength | ASTM D790 | 96.0 Mpa |
| Electrical performance | Test Condition | Test Method | LG CHEM KOREA/1303-07 |
|---|---|---|---|
| Dissipation Factor | 60Hz | ASTM D150 | 1E-03 |
| dielectric constant | 60Hz | ASTM D150 | 3.00 |
| dielectric strength | ASTM D149 | 17 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | 2.00mm | IEC 60112 | PLC 2 |
| volume resistivity | 23°C | ASTM D257 | 2E+17 ohms·cm |
| optical performance | Test Condition | Test Method | LG CHEM KOREA/1303-07 |
|---|---|---|---|
| transmissivity | ASTM D1003 | 89.0 % | |
| refractive index | ASTM D542 | 1.586 | |
| Haze ratio | ASTM D1003 | 0.70to1.5 % |
| Physical properties | Test Condition | Test Method | LG CHEM KOREA/1303-07 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ASTM D570 | 0.32 % |
| 23°C,24hr | ASTM D570 | 0.15 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 7.0 g/10min |
| shrinkage rate | MD | ASTM D955 | 0.50-0.70 % |
| flammability | Test Condition | Test Method | LG CHEM KOREA/1303-07 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| GWIT | 2.0mm | IEC 60695-2-13 | 850 °C |
| Average degree of combustion | ASTM D635 | 3 CM | |
| Limiting Oxygen Index | ASTM D2863 | 26 % | |
| UL flame retardant rating | 0.50mm | UL 94 | HB |