Material Properties:wear resistant｜Good wear resistance
Application Areas:Fitness equipment｜Automotive Applications｜Thin walled products
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
Shrinkage rate		ISO 294-4	1.1 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.90 %
density		ISO 1183	1.51 g/cm³
Melt volume flow rate		ISO 1133	8.00 cm3/10min

Mechanical properties	Test Method	Test Result
Tensile strain	ISO 527-2/1A/50	17 %
Tensile modulus	ISO 527-2/1A/1	2100 Mpa
tensile strength	ISO 527-2/1A/50	44.0 Mpa
Flexural modulus	ISO 178	2050 Mpa

Impact resistance	Test Method	Test Result
Impact strength of cantilever beam gap	ISO 180/1A	4.4 kJ/m²
Impact strength of simply supported beam without notch	ISO 179/1eU	61 kJ/m²
Charpy Notched Impact Strength	ISO 179/1eA	4.0 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
melting temperature		ISO 11357-3	166 °C
Heat distortion temperature		ISO 75-2/A	87.0 °C
Linear coefficient of thermal expansion		ISO 11359-2	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	1.2E-04 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.