Material Description

Material Properties:Easy to form｜Easy to demould
Application Areas:Electronic and Electrical Applications｜Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Multi axis Instrumented Impact Energy		ISO 6603-2	6.80	J
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	23.2	J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	49	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	13	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Wear factor	Washer	ASTM D3702Modified	166	10^-10in^5-min/ft-lb-hr
Friction coefficient	Static	ASTM D3702Modified	0.44
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702Modified	0.38
bending strength		ISO 178	118	Mpa
Bending modulus		ISO 178	3900	Mpa
Bending modulus	Bending modulus		ASTM D790	4140	Mpa
Tensile strain	Break	ISO 527-2	5.8	%
elongation	Break	ASTM D638	5.5	%
Tensile strain	Yield	ISO 527-2	3.3	%
elongation	Yield	ASTM D638	3.3	%
tensile strength	Break	ISO 527-2	67.0	Mpa
	tensile strength	Break	ASTM D638	67.6	Mpa
		tensile strength	Yield	ISO 527-2	71.0	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	71.7	Mpa
Tensile modulus		ISO 527-2/1	4150	Mpa
Tensile modulus	Tensile modulus		ASTM D638	4140	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	145	°C
	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	146	°C
		Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	140	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	140	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	5.6E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	5.6E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	5.6E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	5.6E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD：24hr	ASTM D955	0.60-0.80	%
Shrinkage rate	Shrinkage rate	MD：24hr	ASTM D955	0.40-0.60	%
Water absorption rate	24hr,50%RH	ASTM D570	0.10	%
Shrinkage rate	MD:24hr	ISO 294-4	0.50	%
Shrinkage rate	Shrinkage rate	TD:24hr	ISO 294-4	0.65	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Huizhou Rijing	US$ 5840 /MT

Supplier Join

Get App