PA12 Pebax® 6333 SP 01 ARKEMA USA

460

Unit Price:US$ 15,350 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low temperature resistance｜High temperature resistance
Application Areas:Medical Supplies｜disposable
Color:--
Grade:--

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Melt density			0.830	g/cm³
Thermal conductivity of melt			0.18	W/m/K
Specific Heat Capacity of Melt			2800	J/kg/°C
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level		UL 94	HB
Extreme Oxygen Index		ISO 4589-2	20	%
elastomer	Test Condition	Test Method	Test Result	Test Unit
tear strength		ISO 34-1	130	kN/m
Permanent compression deformation	23°C	ISO 815	47	%
squeeze out	Test Condition	Test Method	Test Result	Test Unit
drying temperature			65 to 75	°C
drying time			4.0 to 6.0	hr
Melt Temperature			210 to 240	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	307	Mpa
tensile strength	Yield	ISO 527-2	19.0	Mpa
	tensile strength	Break	ISO 527-2	53.0	Mpa
		tensile strength	10% Strain	ISO 527-2	14.0	Mpa
		tensile strength	tensile strength	100% Strain	ISO 527-2	17.0	Mpa
Tensile strain	Yield	ISO 527-2	22	%
Tensile strain	Tensile strain	Break	ISO 527-2	> 300	%
Nominal tensile fracture strain		ISO 527-2	> 50	%
Wear resistance		ISO 4649	55.0	mm³
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			65 to 75	°C
drying time			4.0 to 6.0	hr
Processing (melt) temperature			230 to 290	°C
Mold temperature			25 to 60	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	90.0	°C
Vicat softening temperature		ISO 306/B50	157	°C
Melting temperature		ISO 11357-3	169	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.4E-4	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	横向Flow	ISO 294-4	1.4	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	1.2	%
Water absorption rate	Saturation, 23°C	ISO 62	1.1	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.70	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	--	ohms
Volume resistivity		IEC 60093	9.0E+13	ohms·cm
Dielectric strength		IEC 60243-1	43	KV/mm
Relative permittivity	100 Hz	IEC 60250	9.00
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	4.00
Dissipation factor	100 Hz	IEC 60250	0.14
Dissipation factor	Dissipation factor	1 MHz	IEC 60250	0.076
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	Shore D, 15 Sec	ISO 7619-1	58

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Shenzhen Jiuhe	US$ 28190 /MT

Supplier Join

Get App

Top

PA12 Pebax® 6333 SP 01 ARKEMA USA

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index