PA6 6G30UV1 NC DOMO CHEM GERMANY
345
- Unit Price:US$ 2,588 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:93MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ISO 1133 | 45.0 cm3/10min | |
| Shrinkage rate | ISO 2577 | 0.80 - 1.0 % | |
| ISO 2577 | 0.30 - 0.50 % | ||
| viscosity number | ISO 307 | 145 cm³/g |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 122 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | FMVSS 302 | < 100 mm/min | |
| UL flame retardant rating | UL 94 | HB | |
| Burning wire flammability index | IEC 60695-2-12 | 650 °C | |
| ISO 9660 | ISO 1874 | PA6.ML.14-090.GF30 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 9500 Mpa | |
| tensile strength | ISO 527-2/5 | 180 Mpa | |
| Tensile strain | ISO 527-2/5 | 3.5 % | |
| Flexural modulus | ISO 178 | 8500 Mpa | |
| bending strength | ISO 178 | 270 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 90 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180/1U | 80 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1.0E+13 ohms | |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 75 to 85 °C | ||
| drying time | 2.0 to 4.0 hr | ||
| Processing (melt) temperature | 240 to 270 °C | ||
| Temperature | 90 to 100 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 220 °C | |
| ISO 75-2/A | 200 °C | ||
| vicat | ISO 306/B50 | 215 °C | |
| melting temperature | ISO 11357-3 | 221 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.