PA6 6G30UV1 NC DOMO CHEM GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DOMO CHEM GERMANY/6G30UV1 NC |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 80 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 kJ/m² |
| hardness | Test Condition | Test Method | DOMO CHEM GERMANY/6G30UV1 NC |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 122 |
| Mechanical properties | Test Condition | Test Method | DOMO CHEM GERMANY/6G30UV1 NC |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 9500 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 180 Mpa |
| bending strength | ISO 178 | 270 Mpa | |
| Flexural modulus | ISO 178 | 8500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 3.5 % |
| Electrical performance | Test Condition | Test Method | DOMO CHEM GERMANY/6G30UV1 NC |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | V |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | 1.0E+13 ohms |
| flammability | Test Condition | Test Method | DOMO CHEM GERMANY/6G30UV1 NC |
|---|---|---|---|
| burning rate | FMVSS 302 | < 100 mm/min | |
| UL flame retardant rating | 0.8 mm | UL 94 | HB |
| Burning wire flammability index | 1.0 到 3.0 mm | IEC 60695-2-12 | 650 °C |
| ISO 9660 | ISO 1874 | PA6.ML.14-090.GF30 |
| physical property | Test Condition | Test Method | DOMO CHEM GERMANY/6G30UV1 NC |
|---|---|---|---|
| Shrinkage rate | 流量 : 23°C, 72小时 | ISO 2577 | 0.30 - 0.50 % |
| viscosity number | 96% H2SO4 | ISO 307 | 145 cm³/g |
| Melt volume flow rate | 275°C/5.0 kg | ISO 1133 | 45.0 cm3/10min |
| Shrinkage rate | 横向流量 : 23°C, 72小时 | ISO 2577 | 0.80 - 1.0 % |
| Thermal performance | Test Condition | Test Method | DOMO CHEM GERMANY/6G30UV1 NC |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 221 °C | |
| Hot deformation temperature (HDT) | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 220 °C |
| vicat | ISO 306/B50 | 215 °C | |
| Hot deformation temperature (HDT) | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 200 °C |
| injection | Test Condition | Test Method | DOMO CHEM GERMANY/6G30UV1 NC |
|---|---|---|---|
| drying time | 2.0 to 4.0 hr | ||
| Processing (melt) temperature | 240 to 270 °C | ||
| drying temperature | 75 to 85 °C | ||
| Temperature | 90 to 100 °C |