PA66 Leona™ 90G50 ASAHI JAPAN

302

Unit Price:US$ 4,110 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
82.5MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Good appearance｜High rigidity｜Glass fiber reinforced｜enhance
Application Areas:furniture
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch		ISO 179	88	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75mm	UL 94	HB
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	湿		1.1	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C	ISO 178	355	Mpa
bending strength	bending strength		ASTM D790	373	Mpa
Bending modulus	23°C	ISO 178	14200	Mpa
Bending modulus	Bending modulus		ASTM D790	15500	Mpa
Tensile strain	Break,23°C	ISO 527-2	2.0	%
elongation	Break	ASTM D638	2.5	%
tensile strength	Break,23°C	ISO 527-2	250	Mpa
tensile strength	tensile strength		ASTM D638	235	Mpa
Tensile modulus	23°C	ISO 527-2	18000	Mpa
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	127(133)	J/m
flexural coefficient	干(湿)	ASTM D-790	15.5(12.1)	GPa
Rockwell hardness	干(湿)	ASTM D-785	120(-)	R scale
Rockwell hardness	Rockwell hardness	干(湿)	ASTM D-785	90(-)	M Scale
bending strength	干(湿)	ASTM D-790	373(304)	Mpa
tensile strength	干(湿)	ASTM D-638	235(196)	Mpa
Elongation at Break	干(湿)	ASTM D-638	2.5(3)	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	干	ASTM D-696	2
Hot deformation temperature	1.82MPa,干	ASTM D-648	225	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	240	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	225	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	225	°C
Linear coefficient of thermal expansion	MD	ASTM D696	2E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	干	旭化成方法	0.2/0.5	%
	Shrinkage rate	TD	Internal Method	0.50	%
		Shrinkage rate	MD	Internal Method	0.20	%
		Shrinkage rate	Shrinkage rate	吸水率(Saturation,23°C)	Internal Method	--	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	--	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale	ISO 2039-2	100
	Rockwell hardness	R-Sale	ISO 2039-2	120
		Rockwell hardness	R-Sale	ASTM D785	120
		Rockwell hardness	Rockwell hardness	M-Sale	ASTM D785	90

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join