PA66 90G50 ASAHI JAPAN
Leona™
furniture
Good appearance,High rigidity,Glass fiber reinforced,enhance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | ASAHI JAPAN/90G50 |
---|---|---|---|
Impact strength of simply supported beam without notch | ISO 179 | 88 kJ/m² |
hardness | Test Condition | Test Method | ASAHI JAPAN/90G50 |
---|---|---|---|
Rockwell hardness | M计秤 | ASTM D785 | 90 |
R计秤 | ISO 2039-2 | 120 | |
M计秤 | ISO 2039-2 | 100 | |
R计秤 | ASTM D785 | 120 |
Basic performance | Test Condition | Test Method | ASAHI JAPAN/90G50 |
---|---|---|---|
Water absorption rate | 湿 | 1.1 % |
Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/90G50 |
---|---|---|---|
Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 127(133) J/m |
flexural coefficient | 干(湿) | ASTM D-790 | 15.5(12.1) GPa |
bending strength | ASTM D790 | 373 Mpa | |
tensile strength | 干(湿) | ASTM D-638 | 235(196) Mpa |
Tensile modulus | 23°C | ISO 527-2 | 18000 Mpa |
tensile strength | 断裂,23°C | ISO 527-2 | 250 Mpa |
Flexural modulus | ASTM D790 | 15500 Mpa | |
tensile strength | ASTM D638 | 235 Mpa | |
Rockwell hardness | 干(湿) | ASTM D-785 | 120(-) R scale |
干(湿) | ASTM D-785 | 90(-) M Scale | |
elongation | 断裂 | ASTM D638 | 2.5 % |
Tensile strain | 断裂,23°C | ISO 527-2 | 2.0 % |
bending strength | 23°C | ISO 178 | 355 Mpa |
干(湿) | ASTM D-790 | 373(304) Mpa | |
Flexural modulus | 23°C | ISO 178 | 14200 Mpa |
elongation at break | 干(湿) | ASTM D-638 | 2.5(3) % |
flammability | Test Condition | Test Method | ASAHI JAPAN/90G50 |
---|---|---|---|
UL flame retardant rating | 0.75mm | UL 94 | HB |
physical property | Test Condition | Test Method | ASAHI JAPAN/90G50 |
---|---|---|---|
Shrinkage rate | MD | 内部方法 | 0.20 % |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | -- % |
Shrinkage rate | 吸水率(饱和,23°C) | 内部方法 | -- % |
TD | 内部方法 | 0.50 % | |
干 | 旭化成方法 | 0.2/0.5 % |
Thermal performance | Test Condition | Test Method | ASAHI JAPAN/90G50 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 225 °C |
1.82MPa,干,HDT | ASTM D-648 | 225 °C | |
0.45MPa,未退火,HDT | ISO 75-2/B | 240 °C | |
1.8MPa,未退火,HDT | ISO 75-2/A | 225 °C | |
Linear coefficient of thermal expansion | MD | ASTM D696 | 2E-05 cm/cm/°C |
干 | ASTM D-696 | 2 |