PPO

PPO NORYL™ N190X-8C030 SABIC INNOVATIVE SHANGHAI

208

Unit Price:US$ 3,537 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:transparent｜High temperature resistance
Application Areas:Automotive components｜Illuminating lamp
Color:--
Grade:Injection grade

Technical Data Sheet

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	120

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	95.0 °C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Bf	95.0 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	78.0 °C
			Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	86.0 °C
			Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	82.0 °C
Vicat softening temperature	--	ASTM D15259	104 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	107 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.7E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	8.1E-5 cm/cm/°C
thermal conductivity		ASTM C177	0.24 W/m/K
RTI Elec		UL 746	95.0 °C
RTI Imp		UL 746	80.0 °C
RTI		UL 746	95.0 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.0 mm	UL 94	HB
	UL flame retardant rating	1.5 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Extreme Oxygen Index		ASTM D2863	39 %

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	280°C/5.0 kg	ASTM D1238	20 g/10 min
Melt Volume Flow Rate (MVR)	280°C/5.0 kg	ISO 1133	23.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %
Water absorption rate	24 hr	ASTM D570	0.080 %
Outdoor applicability		UL 746C	f1

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	1.8E+16 ohms·cm
Dielectric strength	3.20 mm, in Oil	ASTM D149	19 KV/mm
Dielectric constant	100 Hz	ASTM D150	2.74
Dielectric constant	Dielectric constant	100 kHz	ASTM D150	2.60
Dissipation factor	100 Hz	ASTM D150	0.013
Dissipation factor	Dissipation factor	100 kHz	ASTM D150	5.5E-3
Arc resistance		ASTM D495	PLC 7
Compared to the anti leakage trace index		UL 746	PLC 1
High arc combustion index		UL 746	PLC 2
High voltage arc tracing rate		UL 746	PLC 4
Hot wire ignition		UL 746	PLC 2

injection	Test Condition	Test Method	Test Result
drying temperature			75 to 80 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			30 to 70 %
Temperature at the rear of the barrel			215 to 265 °C
Temperature in the middle of the barrel			225 to 270 °C
Temperature at the front of the material cylinder			240 to 275 °C
Spray nozzle temperature			250 to 275 °C
Processing (melt) temperature			250 to 275 °C
Mold temperature			55 to 75 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			20 to 100 rpm
Exhaust hole depth			0.038 to 0.051 mm

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--2	ASTM D638	2580 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2600 Mpa
tensile strength	Yield3	ASTM D638	60.0 Mpa
	tensile strength	Yield	ISO 527-2/50	58.0 Mpa
		tensile strength	Break3	ASTM D638	47.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	50.0 Mpa
elongation	Yield3	ASTM D638	3.6 %
	elongation	Yield	ISO 527-2/50	3.2 %
		elongation	Break3	ASTM D638	9.0 %
		elongation	elongation	Break	ISO 527-2/50	9.2 %
Bending modulus	50.0 mm Span4	ASTM D790	2500 Mpa
	Bending modulus	100 mm Span5	ASTM D790	2300 Mpa
	Bending modulus	Bending modulus	--6	ISO 178	2350 Mpa
bending strength	--6,7	ISO 178	87.0 Mpa
	bending strength	Yield, 50.0 mm Span4	ASTM D790	98.0 Mpa
	bending strength	bending strength	Yield, 100 mm Span5	ASTM D790	91.0 Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	76.0 mg

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ASTM D4812	720 J/m
Dart impact	23°C, Total Energy	ASTM D3763	50.0 J

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO NORYL™ N190X-8C030 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet