Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO N190X-8C030 SABIC INNOVATIVE SHANGHAI
NORYL™ 
Automotive components、Illuminating lamp
transparent、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/N190X-8C030
Suspended wall beam without notch impact strength23°CASTM D4812720 J/m
Dart impact23°C, Total EnergyASTM D376350.0 J
hardnessTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/N190X-8C030
Rockwell hardnessR 级ASTM D785120
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/N190X-8C030
Tensile modulus--2ASTM D6382580 Mpa
tensile strength 屈服3ASTM D63860.0 Mpa
elongation断裂3ASTM D6389.0 %
bending strength屈服, 100 mm 跨距5ASTM D79091.0 Mpa
Taber abraser1000 Cycles, 1000 g, CS-17 转轮ASTM D104476.0 mg
elongation断裂ISO 527-2/509.2 %
bending strength--6,7ISO 17887.0 Mpa
屈服, 50.0 mm 跨距4ASTM D79098.0 Mpa
Flexural modulus--6ISO 1782350 Mpa
50.0 mm 跨距4ASTM D7902500 Mpa
tensile strength 断裂ISO 527-2/5050.0 Mpa
屈服ISO 527-2/5058.0 Mpa
elongation屈服ISO 527-2/503.2 %
屈服3ASTM D6383.6 %
tensile strength 断裂3ASTM D63847.0 Mpa
Flexural modulus100 mm 跨距5ASTM D7902300 Mpa
Tensile modulus--ISO 527-2/12600 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/N190X-8C030
dielectric constant100 kHzASTM D1502.60
dielectric strength3.20 mm, in OilASTM D14919 KV/mm
Volume resistivityASTM D2571.8E+16 ohms·cm
Dissipation Factor100 HzASTM D1500.013
dielectric constant100 HzASTM D1502.74
Dissipation Factor100 kHzASTM D1505.5E-3
Hot wire ignition (HWI)UL 746PLC 2
arc resistanceASTM D495PLC 7
High Voltage Arc Traceability Rate (HVTR)UL 746PLC 4
Compared to the Leakage Tracking Index (CTI)UL 746PLC 1
High arc combustion index (HAI)UL 746PLC 2
flammabilityTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/N190X-8C030
UL flame retardant rating3.0 mmUL 945VA
1.0 mmUL 94HB
1.5 mmUL 94V-0
Limiting Oxygen IndexASTM D286339 %
physical property Test ConditionTest MethodSABIC INNOVATIVE SHANGHAI/N190X-8C030
melt mass-flow rate280°C/5.0 kgASTM D123820 g/10 min
Outdoor applicabilityUL 746Cf1
Water absorption rate24 hrASTM D5700.080 %
Melt volume flow rate280°C/5.0 kgISO 113323.0 cm3/10min
Shrinkage rate3.20 mm，Flow内部方法0.50 - 0.70 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/N190X-8C030
Heat distortion temperature0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8，HDTISO 75-2/Bf95.0 °C
Linear coefficient of thermal expansion流动 : -40 到 40°CASTM E8317.7E-5 cm/cm/°C
vicat--ASTM D15259104 °C
Heat distortion temperature0.45 MPa, 未退火, 3.20 mm，HDTASTM D64895.0 °C
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8，HDTISO 75-2/Af82.0 °C
RTIUL 74695.0 °C
vicat--ISO 306/B120107 °C
thermal conductivityASTM C1770.24 W/m/K
Heat distortion temperature1.8 MPa, 未退火, 6.40 mm，HDTASTM D64886.0 °C
RTI ImpUL 74680.0 °C
Linear coefficient of thermal expansion横向 : -40 到 40°CASTM E8318.1E-5 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 3.20 mm，HDTASTM D64878.0 °C
RTI ElecUL 74695.0 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/N190X-8C030
screw speed20 to 100 rpm
Suggested maximum moisture content0.020 %
Processing (melt) temperature250 to 275 °C
drying temperature75 to 80 °C
Suggested injection volume30 to 70 %
drying time3.0 to 4.0 hr
Temperature in the middle of the barrel225 to 270 °C
Temperature at the rear of the barrel215 to 265 °C
Exhaust hole depth0.038 to 0.051 mm
Temperature at the front of the material cylinder240 to 275 °C
Back pressure0.300 to 0.700 Mpa
Temperature55 to 75 °C
Spray nozzle temperature250 to 275 °C