PA66 Zytel® FR50 BK505 DUPONT USA
245
- Unit Price:US$ 5,903 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:118MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced
- Application Areas:Fitness equipment｜Automotive sector｜Electrical field｜Electronic field｜Electrical appliances
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 242 °C |
| melting temperature | ISO 11357-3 | 260 °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 2.1E-05 cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 2.5E-05 cm/cm/°C | |
| MD：55to160°C | ISO 11359-2 | 1.2E-05 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 7.9E-05 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 6.9E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| Combustibility (rate) | UL 94 | V-0 | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 242 ℃（℉） |
| melting temperature | 260 ℃（℉） | ||
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 240 °C |
| melting temperature | ISO 11357-3 | 262 °C |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | PA66.25％玻维增强.阻燃.注射成型 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| FMVSS flammability | FMVSS302 | B | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 | |
| 0.75mm | IEC 60695-11-10,-20 | V-0 | |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 35 % | |
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 4.70 µgC/g | |
| Odor | VDA270 | 4.50 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 50 kJ/m² |
| -30°C | ISO 179/1eU | 50 kJ/m² | |
| 23°C | ISO 179/1eU | 60 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ejection Temperature | 210 °C | ||
| shrinkage rate | TD | ISO 294-4 | 0.70 % |
| MD | ISO 294-4 | 0.30 % | |
| density | ASTM D792/ISO 1183 | 1.60 | |
| shrinkage rate | ASTM D955 | 0.3-0.7 % | |
| 横向流量 | ISO 294-4 | 0.80 % | |
| 流量 | ISO 294-4 | 0.30 % | |
| Water absorption rate | 24 hr, 23°C, 2.00 mm | ISO 62 | 0.60 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 62631-3-2 | -- ohms | |
| volume resistivity | IEC 62631-3-1 | > 1.0E+13 ohms·m | |
| dielectric strength | 2.00 mm | IEC 60243-1 | 24 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.20 % | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| Melt Temperature, Optimum | 290 °C | ||
| mold temperature | 70 to 120 °C | ||
| Mold Temperature, Optimum | 100 °C | ||
| pressure holding | 50.0 to 100 Mpa | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 s/mm | ||
| Maximum Screw Tangential Speed | 12 m/min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10600 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 158 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.1 % |
| flexural modulus | ISO 178 | 9410 Mpa | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 8.4 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 7.9 kg·cm/cm(J/M)ft·lb/in | ||
| Elongation at break | ASTM D638/ISO 527 | 2.1 % | |
| Tensile modulus | ASTM D638/ISO 527 | 10640 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 158 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 9410 kg·cm/cm(J/M)ft·lb/in | |
| Tensile modulus | ISO 527-2 | 10200 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 170 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.6 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.