PA66 FR50 BK505 DUPONT USA
Zytel® 
Fitness equipment,Automotive sector,Electrical field,Electronic field,Electrical appliances
Flame retardant,Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDUPONT USA/FR50 BK505
Impact strength of simply supported beam without notch-40°CISO 179/1eU50 kJ/m²
23°CISO 179/1eU60 kJ/m²
-30°CISO 179/1eU50 kJ/m²
Supplementary InformationTest ConditionTest MethodDUPONT USA/FR50 BK505
OdorVDA2704.50
Emissions of Organic CompoundsVDA2774.70 µgC/g
thermal performanceTest ConditionTest MethodDUPONT USA/FR50 BK505
melting temperature260 ℃（℉）
Heat Deflection Temperature1.8 MPa, 未退火，HDTISO 75-2/A240 °C
1.8MPa,未退火，HDTISO 75-2/A242 °C
Linear coefficient of thermal expansionTD：-40to23°CISO 11359-26.9E-05 cm/cm/°C
MD：--ISO 11359-22.1E-05 cm/cm/°C
Heat Deflection TemperatureHDTASTM D648/ISO 75242 ℃（℉）
Linear coefficient of thermal expansionMD：-40to23°CISO 11359-22.5E-05 cm/cm/°C
MD：55to160°CISO 11359-21.2E-05 cm/cm/°C
Combustibility (rate)UL 94V-0
Linear coefficient of thermal expansionTD：--ISO 11359-27.9E-05 cm/cm/°C
TD：55to160°CISO 11359-21.1E-04 cm/cm/°C
melting temperatureISO 11357-3262 °C
mechanical propertiesTest ConditionTest MethodDUPONT USA/FR50 BK505
Tensile modulusASTM D638/ISO 52710640 kg/cm²(MPa)[Lb/in²]
Elongation at breakASTM D638/ISO 5272.1 %
Tensile modulusISO 527-210200 Mpa
tensile strengthASTM D638/ISO 527158 kg/cm²(MPa)[Lb/in²]
断裂ISO 527-2170 Mpa
Tensile strain断裂ISO 527-22.6 %
Impact strength of cantilever beam gapASTM D256/ISO 1797.9 kg·cm/cm(J/M)ft·lb/in
flexural modulusISO 1789410 Mpa
ASTM D790/ISO 1789410 kg·cm/cm(J/M)ft·lb/in
Electrical performanceTest ConditionTest MethodDUPONT USA/FR50 BK505
dielectric strength2.00 mmIEC 60243-124 KV/mm
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 2
volume resistivityIEC 62631-3-1> 1.0E+13 ohms·m
Surface ResistivityIEC 62631-3-2-- ohms
otherTest ConditionTest MethodDUPONT USA/FR50 BK505
characteristicPA66.25％玻维增强.阻燃.注射成型
Physical propertiesTest ConditionTest MethodDUPONT USA/FR50 BK505
shrinkage rate流量ISO 294-40.30 %
ASTM D9550.3-0.7 %
横向流量ISO 294-40.80 %
densityASTM D792/ISO 11831.60
shrinkage rateTDISO 294-40.70 %
Ejection Temperature210 °C
shrinkage rateMDISO 294-40.30 %
Water absorption rate24 hr, 23°C, 2.00 mmISO 620.60 %
flammabilityTest ConditionTest MethodDUPONT USA/FR50 BK505
UL flame retardant rating0.75mmUL 94V-0
0.75mmIEC 60695-11-10,-20V-0
1.5mmIEC 60695-11-10,-20V-0
UL 94V-0
FMVSS flammabilityFMVSS302B
UL flame retardant rating1.5mmUL 94V-0
Limiting Oxygen IndexISO 4589-235 %
burning rate1.00mmISO 3795<100 mm/min
injectionTest ConditionTest MethodDUPONT USA/FR50 BK505
pressure holding50.0 to 100 Mpa
Maximum Screw Tangential Speed12 m/min
pressure holdingDrying Recommendedyes
Suggested maximum moisture content0.20 %
Drying time - hot air dryer2.0 to 4.0 hr
Processing (melt) temperature280 to 300 °C
mold temperature70 to 120 °C
drying temperature80 °C
Melt Temperature, Optimum290 °C
Hold Pressure Time3.00 s/mm
Mold Temperature, Optimum100 °C