PP PRIME E-2900 PRIME POLYMER JAPAN
230
- Unit Price:US$ 1,561 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:27MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 67 |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Haze ratio | 80.0µm3 | JISK7105 | 0.60 % |
| 80.0µm2 | JISK7105 | 11 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 15 kJ/m² |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| film thickness | 80 µm | ||
| Tensile modulus | MD:80µm | JISZ1702 | 430 Mpa |
| TD:80µm | JISZ1702 | 430 Mpa | |
| tensile strength | MD:断裂,80µm | JISZ1702 | 40.0 Mpa |
| TD:断裂,80µm | JISZ1702 | 40.0 Mpa | |
| elongation | MD:断裂,80µm | JISZ1702 | >500 % |
| TD:断裂,80µm | JISZ1702 | >500 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 2.8 g/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2 | 18.0 Mpa |
| 断裂 | ISO 527-2 | 22.5 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | >500 % |
| flexural modulus | ISO 178 | 450 Mpa | |
| bending strength | ISO 178 | 17.5 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.