PP E-2900 PRIME POLYMER JAPAN
PRIME
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | PRIME POLYMER JAPAN/E-2900 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 15 kJ/m² |
| hardness | Test Condition | Test Method | PRIME POLYMER JAPAN/E-2900 |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 67 |
| film | Test Condition | Test Method | PRIME POLYMER JAPAN/E-2900 |
|---|---|---|---|
| elongation | TD:断裂,80µm | JISZ1702 | >500 % |
| film thickness | 80 µm | ||
| Tensile modulus | MD:80µm | JISZ1702 | 430 Mpa |
| tensile strength | MD:断裂,80µm | JISZ1702 | 40.0 Mpa |
| Tensile modulus | TD:80µm | JISZ1702 | 430 Mpa |
| tensile strength | TD:断裂,80µm | JISZ1702 | 40.0 Mpa |
| elongation | MD:断裂,80µm | JISZ1702 | >500 % |
| Mechanical properties | Test Condition | Test Method | PRIME POLYMER JAPAN/E-2900 |
|---|---|---|---|
| bending strength | ISO 178 | 17.5 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | >500 % |
| Flexural modulus | ISO 178 | 450 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 22.5 Mpa |
| 屈服 | ISO 527-2 | 18.0 Mpa |
| optical performance | Test Condition | Test Method | PRIME POLYMER JAPAN/E-2900 |
|---|---|---|---|
| Haze ratio | 80.0µm2 | JISK7105 | 11 % |
| 80.0µm3 | JISK7105 | 0.60 % |
| physical property | Test Condition | Test Method | PRIME POLYMER JAPAN/E-2900 |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 2.8 g/10min |