Plastic Raw Materials
PC

PC LEXAN™ Resin HFD1930 -NA9E109T SABIC INNOVATIVE KOREA

244
  • Unit Price:US$ 4,162 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    18.8MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:--
  • Application Areas:--
  • Color:--
  • Grade:High mobility

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
Refractive indexASTM D5421.582
transmissivity2540 μmASTM D100388.0 %
turbidity2540 μmASTM D1003< 1.0 %
impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact23°C, Total EnergyASTM D376356.0 J
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Charpy Notched Impact Strength23°CISO 179/1eA60 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA11 kJ/m²
Dart impact--ISO 6603-292.0 J
mechanical propertiesTest ConditionTest MethodTest Result
bending strengthYield, 50.0 mm Span4ASTM D790100 Mpa
bending strength--5,6ISO 17890.0 Mpa
Bending modulus--5ISO 1782200 Mpa
Bending modulus50.0 mm Span4ASTM D7902280 Mpa
elongationBreakISO 527-2/50100 %
elongationBreak3ASTM D638110 %
elongationYieldISO 527-2/506.0 %
elongationYield3ASTM D6385.5 %
tensile strengthBreakISO 527-2/5056.0 Mpa
tensile strengthBreak3ASTM D63857.0 Mpa
tensile strengthYieldISO 527-2/5061.0 Mpa
tensile strengthYield3ASTM D63860.0 Mpa
Tensile modulus--ISO 527-2/12200 Mpa
Tensile modulus--2ASTM D6382300 Mpa
injectionTest ConditionTest MethodTest Result
Exhaust hole depth0.038 to 0.076 mm
drying temperature105 to 110 °C
drying time3.0 to 4.0 hr
Suggested injection volume40 to 60 %
Temperature at the rear of the barrel240 to 280 °C
Temperature in the middle of the barrel250 to 295 °C
Temperature at the front of the material cylinder260 to 305 °C
Spray nozzle temperature255 to 300 °C
Processing (melt) temperature260 to 305 °C
Mold temperature50 to 80 °C
Back pressure0.300 to 0.700 Mpa
Screw speed35 to 75 rpm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D648124 °C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648110 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9ISO 75-2/Af120 °C
Vicat softening temperature--ASTM D152510141 °C
Vicat softening temperature--ISO 306/B50135 °C
Vicat softening temperature--ISO 306/B120136 °C
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8318.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8318.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40°CISO 11359-28.0E-5 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.15 %
Water absorption rateSaturation, 23°CISO 620.30 %
Shrinkage rate3.20 mm，FlowInternal Method0.50 - 0.70 %
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 113351.0 cm3/10min
melt mass-flow rate300°C/1.2 kgASTM D123855 g/10 min
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785120
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.