Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HFD1930 -NA9E109T SABIC INNOVATIVE KOREA
LEXAN™ Resin
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE KOREA/HFD1930 -NA9E109T |
|---|---|---|---|
| The impact strength of a simply supported beam without a notch is 7 | 23°C | ISO 179/1eU | 无断裂 |
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 56.0 J |
| Impact strength of simply supported beam gap 7 | -30°C | ISO 179/1eA | 11 kJ/m² |
| Unscented Izod Impact Strength 8 | -30°C | ISO 180/1U | 无断裂 |
| The impact strength of a simply supported beam without a notch is 7 | -30°C | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam gap 7 | 23°C | ISO 179/1eA | 60 kJ/m² |
| Unscented Izod Impact Strength 8 | 23°C | ISO 180/1U | 无断裂 |
| Dart impact equipped with measuring instruments | -- | ISO 6603-2 | 92.0 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE KOREA/HFD1930 -NA9E109T |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE KOREA/HFD1930 -NA9E109T |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 61.0 Mpa |
| Bending stress | -- 5, 6 | ISO 178 | 90.0 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 100 % |
| Flexural modulus | -- 5 | ISO 178 | 2200 Mpa |
| elongation | 屈服 3 | ASTM D638 | 5.5 % |
| Bending stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 100 Mpa |
| Tensile modulus | -- 2 | ASTM D638 | 2300 Mpa |
| tensile strength | 屈服 3 | ASTM D638 | 60.0 Mpa |
| 断裂 | ISO 527-2/50 | 56.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 6.0 % |
| Flexural modulus | 50.0 mm 跨距 4 | ASTM D790 | 2280 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2200 Mpa |
| elongation | 断裂 3 | ASTM D638 | 110 % |
| tensile strength | 断裂 3 | ASTM D638 | 57.0 Mpa |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE KOREA/HFD1930 -NA9E109T |
|---|---|---|---|
| refractive index | ASTM D542 | 1.582 | |
| transmissivity | 2540 µm | ASTM D1003 | 88.0 % |
| Haze ratio | 2540 µm | ASTM D1003 | < 1.0 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE KOREA/HFD1930 -NA9E109T |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| Molten Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 51.0 cm3/10min |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 55 g/10 min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.30 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE KOREA/HFD1930 -NA9E109T |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 136 °C |
| -- | ASTM D152510 | 141 °C | |
| 横向 : -40 到 40°C | ASTM E831 | 8.0E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 110 °C |
| Ball Pressure Test | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9 | ISO 75-2/Af | 120 °C |
| vicat | -- | ISO 306/B50 | 135 °C |
| 横向 : -40°C | ISO 11359-2 | 8.0E-5 cm/cm/°C | |
| 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 8.0E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 124 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE KOREA/HFD1930 -NA9E109T |
|---|---|---|---|
| Temperature | 50 到 80 °C | ||
| screw speed | 35 到 75 rpm | ||
| Temperature at the rear of the barrel | 240 到 280 °C | ||
| Processing (melt) temperature | 260 到 305 °C | ||
| Back pressure | 0.300 到 0.700 Mpa | ||
| drying temperature | 105 到 110 °C | ||
| Exhaust hole depth | 0.038 到 0.076 mm | ||
| Temperature at the front of the material cylinder | 260 到 305 °C | ||
| drying time | 3.0 到 4.0 hr | ||
| Suggested injection volume | 40 到 60 % | ||
| Spray nozzle temperature | 255 到 300 °C | ||
| Temperature in the middle of the barrel | 250 到 295 °C |