Material Description

Material Properties:High mobility｜transparent｜High temperature resistance
Application Areas:Casters｜Sports Equipment
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	11 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	72.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	HB
Burning wire flammability index	3.0 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	875 °C
Metallic haze	起始	Internal Method	175 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--2	ASTM D638	2730 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2750 Mpa
tensile strength	Yield3	ASTM D638	77.0 Mpa
	tensile strength	Yield	ISO 527-2/50	78.0 Mpa
		tensile strength	Break3	ASTM D638	69.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	67.0 Mpa
elongation	Yield3	ASTM D638	7.0 %
	elongation	Yield	ISO 527-2/50	7.0 %
		elongation	Break3	ASTM D638	50 %
		elongation	elongation	Break	ISO 527-2/50	50 %
Bending modulus	50.0 mm Span4	ASTM D790	2600 Mpa
Bending modulus	Bending modulus	--5	ISO 178	2600 Mpa
bending strength	--5,6	ISO 178	80.0 Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	120 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			135 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			280 to 325 °C
Temperature in the middle of the barrel			290 to 335 °C
Temperature at the front of the material cylinder			300 to 345 °C
Spray nozzle temperature			295 to 340 °C
Processing (melt) temperature			300 to 345 °C
Mold temperature			95 to 130 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 90 rpm
Exhaust hole depth			0.025 to 0.080 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	174 °C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Bf	173 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	165 °C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	162 °C
Vicat softening temperature	--	ASTM D152510	183 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	181 °C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Ball Pressure Test	Ball Pressure Test	163 to 167°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.0E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.0E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	6.0E-5 cm/cm/°C
thermal conductivity	25°C	ASTM C177	0.20 W/m/K
RTI Elec		UL 746	150 °C
RTI Imp		UL 746	130 °C
RTI		UL 746	150 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	330°C/2.16 kg	ASTM D1238	25 g/10 min
Melt Volume Flow Rate (MVR)	330°C/2.16 kg	ISO 1133	24.0 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.60 - 0.95 %
Water absorption rate	Saturation, 23°C	ISO 62	0.50 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.25 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257	> 1.0E+17 ohms
Volume resistivity		ASTM D257	> 1.0E+17 ohms·cm
Dielectric constant	100 Hz	ASTM D150	3.12
Dielectric constant	Dielectric constant	1 MHz	ASTM D150	3.02
High arc combustion index		UL 746	PLC 0
Hot wire ignition		UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.