Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC XHT4141-GY8D046 SABIC INNOVATIVE US
LEXAN™ 
Casters、Sports Equipment
High mobility、transparent、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/XHT4141-GY8D046
Charpy Notched Impact Strength23°CISO 179/1eA11 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Charpy Notched Impact Strength-30°CISO 179/1eA9.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact23°C, Total EnergyASTM D376372.0 J
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/XHT4141-GY8D046
Tensile modulus--2ASTM D6382730 Mpa
tensile strength 屈服3ASTM D63877.0 Mpa
elongation断裂3ASTM D63850 %
断裂ISO 527-2/5050 %
Flexural modulus--5ISO 1782600 Mpa
bending strength屈服, 50.0 mm 跨距4ASTM D790120 Mpa
--5,6ISO 17880.0 Mpa
Flexural modulus50.0 mm 跨距4ASTM D7902600 Mpa
tensile strength 断裂ISO 527-2/5067.0 Mpa
屈服ISO 527-2/5078.0 Mpa
elongation屈服ISO 527-2/507.0 %
屈服3ASTM D6387.0 %
tensile strength 断裂3ASTM D63869.0 Mpa
Tensile modulus--ISO 527-2/12750 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/XHT4141-GY8D046
Volume resistivityASTM D257> 1.0E+17 ohms·cm
dielectric constant100 HzASTM D1503.12
Surface ResistivityASTM D257> 1.0E+17 ohms
dielectric constant1 MHzASTM D1503.02
Hot wire ignition (HWI)UL 746PLC 3
High arc combustion index (HAI)UL 746PLC 0
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/XHT4141-GY8D046
UL flame retardant rating3.0 mmUL 94HB
Hot filament ignition temperature3.0 mmIEC 60695-2-13875 °C
Burning wire flammability index3.0 mmIEC 60695-2-12960 °C
UL flame retardant rating1.5 mmUL 94HB
Metallic haze起始内部方法175 °C
physical property Test ConditionTest MethodSABIC INNOVATIVE US/XHT4141-GY8D046
Water absorption rate平衡, 23°C, 50% RHISO 620.25 %
melt mass-flow rate330°C/2.16 kgASTM D123825 g/10 min
Water absorption rate饱和, 23°CISO 620.50 %
Melt volume flow rate330°C/2.16 kgISO 113324.0 cm3/10min
Shrinkage rate3.20 mm，Flow内部方法0.60 - 0.95 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/XHT4141-GY8D046
Linear coefficient of thermal expansion流动 : -40 到 40°CASTM E8316.0E-5 cm/cm/°C
thermal conductivity25°CASTM C1770.20 W/m/K
Linear coefficient of thermal expansion横向 : -40°CISO 11359-26.0E-5 cm/cm/°C
Heat distortion temperature0.45 MPa, 未退火, 3.20 mm，HDTASTM D648174 °C
ball-indentation hardness123 到 127°CIEC 60695-10-2通过
Heat distortion temperature0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9，HDTISO 75-2/Bf173 °C
RTIUL 746150 °C
ball-indentation hardness163 到 167°CIEC 60695-10-2通过
vicat--ISO 306/B120181 °C
--ASTM D152510183 °C
Heat distortion temperature1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9，HDTISO 75-2/Af162 °C
RTI ImpUL 746130 °C
Linear coefficient of thermal expansion横向 : -40 到 40°CASTM E8316.0E-5 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 3.20 mm，HDTASTM D648165 °C
RTI ElecUL 746150 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE US/XHT4141-GY8D046
screw speed40 to 90 rpm
Suggested maximum moisture content0.020 %
Processing (melt) temperature300 to 345 °C
drying temperature135 °C
Suggested injection volume40 to 60 %
drying time4.0 to 6.0 hr
Temperature in the middle of the barrel290 to 335 °C
Temperature at the rear of the barrel280 to 325 °C
Exhaust hole depth0.025 to 0.080 mm
Temperature at the front of the material cylinder300 to 345 °C
Back pressure0.300 to 0.700 Mpa
Temperature95 to 130 °C
Spray nozzle temperature295 to 340 °C