PEI ULTEM™ 2210EPR SABIC INNOVATIVE US
255
- Unit Price:US$ 6,635 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜High mobility
- Application Areas:Automotive components｜Casters
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI Str | UL 746 | 105 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTM D648 | 209 °C |
| vicat | ASTM D15256 | 210 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 3.6E-05 cm/cm/°C |
| RTI Imp | UL 746 | 105 °C | |
| RTI Elec | UL 746 | 105 °C | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 214 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 206 °C | |
| 0.45MPa,未退火,3.20mm | ASTM D648 | 211 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.41mm | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 14.9 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| arc resistance | ASTM D495 | PLC6 | |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| TD：3.20mm | 内部方法 | 0.50-0.70 % | |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 13 g/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 3.0 % |
| 屈服 | ASTM D638 | 3.0 % | |
| tensile strength | 断裂 | ASTM D638 | 138 Mpa |
| Tensile modulus | ASTM D638 | 6890 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 138 Mpa |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 207 Mpa |
| Break,100mmSpan | ASTM D790 | 207 Mpa | |
| flexural modulus | 100mmSpan4 | ASTM D790 | 6890 Mpa |
| 50.0mm跨距5 | ASTM D790 | 6890 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.