PEI 2210EPR SABIC INNOVATIVE US
ULTEM™
Automotive components、Casters
Thermal stability、High mobility
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/2210EPR |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 14.9 J |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/2210EPR |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/2210EPR |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 6890 Mpa | |
| elongation | 断裂 | ASTM D638 | 3.0 % |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 207 Mpa |
| elongation | 屈服 | ASTM D638 | 3.0 % |
| bending strength | Break,100mmSpan | ASTM D790 | 207 Mpa |
| Flexural modulus | 100mmSpan4 | ASTM D790 | 6890 Mpa |
| 50.0mm跨距5 | ASTM D790 | 6890 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 138 Mpa |
| 屈服 | ASTM D638 | 138 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/2210EPR |
|---|---|---|---|
| UL flame retardant rating | 0.41mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/2210EPR |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| TD：3.20mm | 内部方法 | 0.50-0.70 % | |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 13 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/2210EPR |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 209 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
| vicat | ASTM D15256 | 210 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 3.6E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 211 °C |
| RTI Imp | UL 746 | 105 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 214 °C |
| RTI Str | UL 746 | 105 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 206 °C |
| RTI Elec | UL 746 | 105 °C |