TPEE Hytrel® 4068 DUPONT USA
330
- Unit Price:US$ 5,430 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:71MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜Aging resistance
- Application Areas:Casters｜medical care
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 8.5 g/10min | |
| MediumDensity | 1.03 g/cm³ | ||
| SpecificHeatCapacity of Melt | 2140 J/kg/°C | ||
| ThermalConductivityofMelt | 0.16 W/m/K | ||
| Melt volume flow rate | ISO 1133 | 8.80 cm3/10min | |
| Shrinkage rate | ISO 294-4 | 0.80 % | |
| ISO 294-4 | 0.80 % | ||
| Water absorption rate | ISO 62 | 0.70 % | |
| ISO 62 | 0.70 % | ||
| ISO 62 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ISO 868 | 37 | |
| ISO 868 | 33 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | ISO 3795 | <100 mm/min | |
| FMVSS flammability | FMVSS302 | B |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 10.0 µgC/g | |
| Odor | VDA270 | 4.00 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| ISO 179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | ISO 8256/1 | 145 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 6.70 Mpa | |
| ISO 527-2 | 7.50 Mpa | ||
| Tensile strain | ISO 527-2 | >300 % | |
| Nominal tensile fracture strain | ISO 527-2 | 800 % | |
| Tensile creep modulus | ISO 899-1 | 28.0 Mpa | |
| ISO 899-1 | 21.0 Mpa | ||
| Flexural modulus | ISO 178 | 45.0 Mpa | |
| wear resistance | ISO 4649 | 180 mm³ | |
| Tensile modulus | ISO 527-2 | 45.0 Mpa | |
| tensile strength | ISO 527-2 | 29.0 Mpa | |
| ISO 527-2 | 2.40 Mpa | ||
| ISO 527-2 | 3.20 Mpa |
| elastomer | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tear strength | ISO 34-1 | 100 kN/m | |
| ISO 34-1 | 100 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 18 KV/mm | |
| relative permittivity | IEC 60250 | 4.80 | |
| IEC 60250 | 4.70 | ||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glass Transition Temperature | ISO 11357-2 | -55.0 °C | |
| melting temperature | ISO 11357-3 | 193 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 2.3E-04 cm/cm/°C | |
| ISO 11359-2 | 2.3E-04 cm/cm/°C | ||
| Effective thermal diffusivity coefficient | 5.44E-08 m²/s |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.