PC/PBT Pocan®  DPCF2200 LANXESS GERMANY

298
  • Unit Price:US$ 2,964 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    85MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:--
  • Application Areas:--
  • Color:--
  • Grade:Flame retardant grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength23℃23°CISO 180/1UNo Break
Suspended wall beam without notch impact strength-30℃-30°CISO 180/1U150 kJ/m²
Impact strength of cantilever beam gap23℃23°CISO 180-1A10 kJ/m²
Impact strength of cantilever beam gap0℃0°CISO 180-1A11 kJ/m²
Impact strength of cantilever beam gap-30℃-30°CISO 180-1A< 10 kJ/m²
Impact strength of simply supported beam without notch23℃23°CISO 179/1eUNo Break
Impact strength of simply supported beam without notch-30℃-30°CISO 179/1eU170 kJ/m²
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus23℃23℃ISO 527-1-22400 Mpa
tensile strengthYield，23℃Yield，23℃ISO 527-2/5045 Mpa
Tensile strainYield，23℃Yield，23℃ISO 527-2/502.9 %
Nominal tensile fracture strain23℃23℃ISO 527-2/50> 15 %
Bending modulus23℃23℃4ISO 178-A2500 Mpa
bending strength3.50% Strain3.5% StrainISO 178-A70 Mpa
bending strength23℃23°CISO 17875 Mpa
Bending strain5 %
Ball Pressure TestISO 2039-1104 Mpa
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionMD：23~55℃MD：23 to 55℃ISO 11359-20.000080 1/℃
Linear coefficient of thermal expansionTD：23~55℃TD：23 to 55℃ISO 11359-20.00010 1/℃
Melting temperatureISO 11357-3225 °C
Ball indentation test115℃115℃IEC 60695-10-2Pass
Vicat softening temperatureB120B120ISO 306/B120118 °C
Hot deformation temperature0.45 MPa，Unannealed0.45 MPa，UnannealedISO 75-2/B95 °C
Hot deformation temperature1.8 MPa，Unannealed1.8 MPa，UnannealedISO 75-2/A75 °C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateMD：120℃，2.0 mm，2 hrsFlow : 120°C, 2 hr, 2.00 mm 33ISO 294-40.5 %
Shrinkage rateMD：250℃，2.0 mmFlow : 482°F, 0.0787 in 22ISO 294-40.9 %
Shrinkage rateTD：120℃，2.0 mm，2 hrsAcross Flow : 120°C, 2 hr, 2.00 mm 33ISO 294-40.5 %
Shrinkage rateTD：250℃，2.0 mmAcross Flow : 482°F, 0.0787 in 22ISO 294-40.9 %
Melt Volume Flow Rate (MVR)260℃，5 kg260℃/5.0 kgISO 113315 cm3/10min
Apparent densityISO 600.8 g/cm³
densityISO 11831.31 g/cm³
Electrical performanceTest ConditionTest MethodTest Result
Dissipation factor23℃，1 MHz23°C, 1 MHzIEC 602500.014
Compared to the anti leakage trace indexSolution ASolution AIEC 60112 V
Dissipation factor23℃，100 Hz23°C, 100 HzIEC 602500.025
Relative permittivity23℃，1 MHz23°C, 1 MHzIEC 602502.9
Relative permittivity23℃，100 Hz23°C, 100 HzIEC 602503.3
flame retardant performanceTest ConditionTest MethodTest Result
UL flame retardant rating0.75 mmUL 94V-0
Glow wire combustion index (GWFI)0.80 mm0.8 mmIEC 60695-2-12960 °C
Ignition temperature of heating wire0.8 mm0.8 mmIEC 60695-2-13800 °C
Ignition temperature of heating wire1.6 mm1.6 mmIEC 60695-2-13800 °C
Ignition temperature of heating wire3 mm3.0 mmIEC 60695-2-13800 °C
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.