PC/PBT DPCF2200 LANXESS GERMANY
Pocan®
--
--
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LANXESS GERMANY/DPCF2200 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23℃23°C | ISO 180-1A | 10 kJ/m² |
| Suspended wall beam without notch impact strength | -30℃-30°C | ISO 180/1U | 150 kJ/m² |
| Impact strength of simply supported beam without notch | -30℃-30°C | ISO 179/1eU | 170 kJ/m² |
| Suspended wall beam without notch impact strength | 23℃23°C | ISO 180/1U | No Break |
| Impact strength of cantilever beam gap | 0℃0°C | ISO 180-1A | 11 kJ/m² |
| -30℃-30°C | ISO 180-1A | < 10 kJ/m² | |
| Impact strength of simply supported beam without notch | 23℃23°C | ISO 179/1eU | No Break |
| Electrical performance | Test Condition | Test Method | LANXESS GERMANY/DPCF2200 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A解决方案 A | IEC 60112 | V |
| Dissipation Factor | 23℃，1 MHz23°C, 1 MHz | IEC 60250 | 0.014 |
| relative permittivity | 23℃，1 MHz23°C, 1 MHz | IEC 60250 | 2.9 |
| 23℃，100 Hz23°C, 100 Hz | IEC 60250 | 3.3 | |
| Dissipation Factor | 23℃，100 Hz23°C, 100 Hz | IEC 60250 | 0.025 |
| Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/DPCF2200 |
|---|---|---|---|
| Tensile strain | 屈服，23℃屈服，23℃ | ISO 527-2/50 | 2.9 % |
| bending strength | 3.50% 应变3.5% Strain | ISO 178-A | 70 Mpa |
| 23℃23°C | ISO 178 | 75 Mpa | |
| Bending Strain | 5 % | ||
| ball-indentation hardness | ISO 2039-1 | 104 Mpa | |
| Nominal tensile fracture strain | 23℃23℃ | ISO 527-2/50 | > 15 % |
| Tensile modulus | 23℃23℃ | ISO 527-1-2 | 2400 Mpa |
| tensile strength | 屈服，23℃屈服，23℃ | ISO 527-2/50 | 45 Mpa |
| Flexural modulus | 23℃23℃4 | ISO 178-A | 2500 Mpa |
| Flame retardant performance | Test Condition | Test Method | LANXESS GERMANY/DPCF2200 |
|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-0 |
| GWIT | 1.6 mm1.6 mm | IEC 60695-2-13 | 800 °C |
| 3 mm3.0 mm | IEC 60695-2-13 | 800 °C | |
| 0.8 mm0.8 mm | IEC 60695-2-13 | 800 °C | |
| Glow wire combustion index (GWFI) | 0.80 mm0.8 mm | IEC 60695-2-12 | 960 °C |
| physical property | Test Condition | Test Method | LANXESS GERMANY/DPCF2200 |
|---|---|---|---|
| Apparent density | ISO 60 | 0.8 g/cm³ | |
| Shrinkage rate | TD：120℃，2.0 mm，2 hrsAcross Flow : 120°C, 2 hr, 2.00 mm 33 | ISO 294-4 | 0.5 % |
| Melt volume flow rate | 260℃，5 kg260℃/5.0 kg | ISO 1133 | 15 cm3/10min |
| Shrinkage rate | MD：250℃，2.0 mmFlow : 482°F, 0.0787 in 22 | ISO 294-4 | 0.9 % |
| density | ISO 1183 | 1.31 g/cm³ | |
| Shrinkage rate | TD：250℃，2.0 mmAcross Flow : 482°F, 0.0787 in 22 | ISO 294-4 | 0.9 % |
| MD：120℃，2.0 mm，2 hrsFlow : 120°C, 2 hr, 2.00 mm 33 | ISO 294-4 | 0.5 % |
| Thermal performance | Test Condition | Test Method | LANXESS GERMANY/DPCF2200 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225 °C | |
| Heat distortion temperature | 0.45 MPa，未退火0.45 MPa，未退火，HDT | ISO 75-2/B | 95 °C |
| 1.8 MPa，未退火1.8 MPa，未退火，HDT | ISO 75-2/A | 75 °C | |
| Linear coefficient of thermal expansion | MD：23~55℃MD：23 到 55℃ | ISO 11359-2 | 0.000080 1/℃ |
| vicat | B120B120 | ISO 306/B120 | 118 °C |
| Ball indentation test | 115℃115℃ | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | TD：23~55℃TD：23 到 55℃ | ISO 11359-2 | 0.00010 1/℃ |