PPA Zytel® HTNFE8200 NC010 DUPONT USA

215

Unit Price:US$ 6,035 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
93.9MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low water absorption｜Non enhanced｜Fatigue resistance｜Heat resistant shock｜High impact｜Low temperature impact resistance｜Low temperature toughness｜Heat aging｜Chemical resistance
Application Areas:Fasteners｜Engine accessories｜Automotive components｜Outdoor sports applications｜Electronic and Electrical Applications｜building
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak

flammability	Test Condition	Test Method	Test Result
Burning rate	1.00mm	ISO 3795	<100 mm/min
UL flame retardant rating	0.75mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	0.75mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	2200 Mpa
tensile strength	Yield	ISO 527-2	68.0 Mpa
Tensile strain	Yield	ISO 527-2	5.5 %
Nominal tensile fracture strain		ISO 527-2	14 %
Bending modulus		ISO 178	2100 Mpa
Poisson's ratio		ISO 527	0.38

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	138 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	126 °C
Melting temperature		ISO 11357-3	300 °C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	9E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	9E-05 cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO 11359-2	1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	9E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD	ISO 294-4	0.90 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.80 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	6.3 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	1.9 %
MediumDensity			0.970 g/cm³
Top out temperature			225 °C
SpecificHeatCapacity of Melt			2220 J/kg/°C
ThermalConductivityofMelt			0.18 W/m/K

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	-- ohms
Volume resistivity		IEC 60093	1E+15 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.