PPA HTNFE8200 NC010 DUPONT USA
Zytel®
Fasteners、Engine accessories、Automotive components、Outdoor sports applicatio、Electronic and Electrical、building
Low water absorption、Non enhanced、Fatigue resistance、Heat resistant shock、High impact、Low temperature impact re、Low temperature toughness、Heat aging、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/HTNFE8200 NC010 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| Electrical performance | Test Condition | Test Method | DUPONT USA/HTNFE8200 NC010 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | -- ohms |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/HTNFE8200 NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2200 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 14 % | |
| Flexural modulus | ISO 178 | 2100 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 5.5 % |
| tensile strength | 屈服 | ISO 527-2 | 68.0 Mpa |
| Poisson's ratio | ISO 527 | 0.38 |
| flammability | Test Condition | Test Method | DUPONT USA/HTNFE8200 NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/HTNFE8200 NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 0.90 % |
| MD | ISO 294-4 | 0.80 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 6.3 % |
| MediumDensity | 0.970 g/cm³ | ||
| Ejection Temperature | 225 °C | ||
| SpecificHeatCapacity of Melt | 2220 J/kg/°C | ||
| ThermalConductivityofMelt | 0.18 W/m/K | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.9 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/HTNFE8200 NC010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 300 °C | |
| Linear coefficient of thermal expansion | TD：-- | ISO 11359-2 | 1E-04 cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| MD：-- | ISO 11359-2 | 9E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 138 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 126 °C |