Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

Filling analysis	Test Method	Test Result
Melt density		1.03 g/cm³
Top out temperature		210 °C
Specific Heat Capacity of Melt		2590 J/kg/°C
Thermal Conductivity of Melt		0.17 W/m/K
Odor	VDA 270	5.00

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0
UL flame retardant rating	UL flame retardant rating		UL 94	V-0
Burning wire flammability index	0.40 mm	IEC 60695-2-12	960 °C
	Burning wire flammability index	0.75 mm	IEC 60695-2-12	960 °C
		Burning wire flammability index	1.5 mm	IEC 60695-2-12	960 °C
		Burning wire flammability index	Burning wire flammability index	3.0 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	0.40 mm	IEC 60695-2-13	960 °C
	Hot filament ignition temperature	0.75 mm	IEC 60695-2-13	960 °C
		Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	960 °C
		Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	960 °C
Extreme Oxygen Index		ISO 4589-2	39 %
FMVSS combustion rate		FMVSS 302	DNI

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	3800 Mpa
tensile strength	Yield	ISO 527-2	-- Mpa
tensile strength	tensile strength	Break	ISO 527-2	80.0 Mpa
Tensile strain	Yield	ISO 527-2	-- %
Tensile strain	Tensile strain	Break	ISO 527-2	10 %
Nominal tensile fracture strain		ISO 527-2	-- %

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
Drying time - hot air dryer			2.0 to 4.0 hr
Suggested maximum moisture content			0.20 %
Processing (melt) temperature			270 to 290 °C
Melt Temperature, Optimum			280 °C
Mold temperature			50 to 90 °C
Mold Temperature, Optimum			70 °C
Maintain pressure			50.0 to 100 Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00 s/mm
Maximum Screw Tangential Speed			12 m/min

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	230 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	80.0 °C
Melting temperature		ISO 11357-3	260 °C
Ball Pressure Test		IEC 60309-1	220 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	横向Flow	ISO 294-4	1.0 %
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.90 %
Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	8.0 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	2.4 %
Stickiness		ISO 307	160 cm³/g

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 62631-3-2	-- ohms
Dielectric strength		IEC 60243-1	31 KV/mm
Compared to the anti leakage trace index		UL 746	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index		IEC 60112	PLC 0

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H 358/30	ISO 2039-1	-- Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 FR7026V0FNC010 DUPONT SHENZHEN

Material Description

Technical Data Sheet Compare

Technical Data Sheet