PA66 FR7026V0FNC010 DUPONT SHENZHEN
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDUPONT SHENZHEN/FR7026V0FNC010
Impact strength of simply supported beam without notch23°CISO 179/1eU80 kJ/m²
hardnessTest ConditionTest MethodDUPONT SHENZHEN/FR7026V0FNC010
ball-indentation hardnessH 358/30ISO 2039-1-- Mpa
Mechanical propertiesTest ConditionTest MethodDUPONT SHENZHEN/FR7026V0FNC010
Tensile modulusISO 527-23800 Mpa
Nominal tensile fracture strainISO 527-2-- %
Tensile strain断裂ISO 527-210 %
屈服ISO 527-2-- %
tensile strength 断裂ISO 527-280.0 Mpa
屈服ISO 527-2-- Mpa
Electrical performanceTest ConditionTest MethodDUPONT SHENZHEN/FR7026V0FNC010
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 0
dielectric strengthIEC 60243-131 KV/mm
Surface ResistivityIEC 62631-3-2-- ohms
Compared to the Leakage Tracking Index (CTI)UL 746PLC 0
flammabilityTest ConditionTest MethodDUPONT SHENZHEN/FR7026V0FNC010
Hot filament ignition temperature1.5 mmIEC 60695-2-13960 °C
Burning wire flammability index0.75 mmIEC 60695-2-12960 °C
Hot filament ignition temperature3.0 mmIEC 60695-2-13960 °C
UL flame retardant ratingUL 94V-0
Hot filament ignition temperature0.40 mmIEC 60695-2-13960 °C
Burning wire flammability index3.0 mmIEC 60695-2-12960 °C
Hot filament ignition temperature0.75 mmIEC 60695-2-13960 °C
Limiting Oxygen IndexISO 4589-239 %
Burning wire flammability index1.5 mmIEC 60695-2-12960 °C
FMVSS combustion rateFMVSS 302DNI
Burning wire flammability index0.40 mmIEC 60695-2-12960 °C
Filling analysisTest ConditionTest MethodDUPONT SHENZHEN/FR7026V0FNC010
Ejection Temperature210 °C
OdorVDA 2705.00
Thermal Conductivity of Melt0.17 W/m/K
Melt density1.03 g/cm³
Specific Heat Capacity of Melt2590 J/kg/°C
physical property Test ConditionTest MethodDUPONT SHENZHEN/FR7026V0FNC010
Water absorption rate饱和, 23°C, 2.00 mmISO 628.0 %
平衡, 23°C, 2.00 mm, 50% RHISO 622.4 %
viscosity numberISO 307160 cm³/g
Shrinkage rate流量ISO 294-40.90 %
横向流量ISO 294-41.0 %
Thermal performanceTest ConditionTest MethodDUPONT SHENZHEN/FR7026V0FNC010
melting temperatureISO 11357-3260 °C
Heat distortion temperature0.45 MPa, 未退火，HDTISO 75-2/B230 °C
1.8 MPa, 未退火，HDTISO 75-2/A80.0 °C
ball-indentation hardnessIEC 60309-1220 °C
injectionTest ConditionTest MethodDUPONT SHENZHEN/FR7026V0FNC010
pressure holding50.0 to 100 Mpa
Maximum Screw Tangential Speed12 m/min
pressure holdingDrying Recommendedyes
Suggested maximum moisture content0.20 %
Drying time - hot air dryer2.0 to 4.0 hr
Processing (melt) temperature270 to 290 °C
drying temperature80 °C
Temperature50 to 90 °C
Melt Temperature, Optimum280 °C
Hold Pressure Time3.00 s/mm
Mold Temperature, Optimum70 °C