ASA/PA SCHULABLEND® M/MW NC100 A SCHULMAN USA
336
- Unit Price:US$ 2,542 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ball Pressure Test | H358/10 | ISO 2039-1 | 101 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vicat softening temperature | -- | ISO 306/B50 | 110 °C |
| -- | ISO 306/A50 | 184 °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/Af | 78.0 °C |
| 0.45MPa,Unannealed | ISO 75-2/Bf | 96.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning rate | ISO 3795 | 30 mm/min | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 700 °C |
| 1.5mm | IEC 60695-2-13 | 700 °C | |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 675 °C |
| 1.5mm | IEC 60695-2-12 | 675 °C | |
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | IEC 60695-11-10,-20 | HB |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Volume Flow Rate (MVR) | 250°C/5.0kg | ISO 1133 | 6.00 cm3/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | Yield | ISO 527-2/1A/50 | 3.1 % |
| tensile strength | Yield | ISO 527-2/1A/50 | 51.0 Mpa |
| Tensile modulus | ISO 527-2/1A/1 | 3100 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| -30°C | ISO 179/1eU | 75 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.