ASA/PA M/MW NC100 A SCHULMAN USA
SCHULABLEND®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | A SCHULMAN USA/M/MW NC100 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| -30°C | ISO 179/1eU | 75 kJ/m² |
| hardness | Test Condition | Test Method | A SCHULMAN USA/M/MW NC100 |
|---|---|---|---|
| ball-indentation hardness | H358/10 | ISO 2039-1 | 101 Mpa |
| Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/M/MW NC100 |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 3.1 % |
| Tensile modulus | ISO 527-2/1A/1 | 3100 Mpa | |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 51.0 Mpa |
| flammability | Test Condition | Test Method | A SCHULMAN USA/M/MW NC100 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 675 °C |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 675 °C |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 700 °C |
| burning rate | ISO 3795 | 30 mm/min | |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 700 °C |
| physical property | Test Condition | Test Method | A SCHULMAN USA/M/MW NC100 |
|---|---|---|---|
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 6.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | A SCHULMAN USA/M/MW NC100 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 78.0 °C |
| vicat | -- | ISO 306/A50 | 184 °C |
| -- | ISO 306/B50 | 110 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 96.0 °C |