'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC LEXAN™ BPL1000 BK SABIC INNOVATIVE US
284
- Unit Price:US$ 4,040 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:65.9MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:UV resistance｜Hydrolysis resistance
- Application Areas:Automotive components｜Electronic and electrical accessories｜Thin walled products
- Color:--
- Grade:Injection grade
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 48.6 | J |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 18 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 12 | kJ/m² |
| 23°C | ISO 180/1A | 18 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.45mm | UL 94 | V-2 | |
| 0.8mm | UL 94 | V-0 | ||
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 800 | °C |
| Extreme Oxygen Index | ISO 4589-2 | 36 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | ASTM D638 | 2680 | Mpa | |
| ISO 527-2/1 | 2460 | Mpa | ||
| tensile strength | Yield | ASTM D638 | 63.4 | Mpa |
| Yield | ISO 527-2/50 | 64.8 | Mpa | |
| Break | ASTM D638 | 51.0 | Mpa | |
| Break | ISO 527-2/50 | 53.5 | Mpa | |
| elongation | Yield | ASTM D638 | 4.8 | % |
| Tensile strain | Yield | ISO 527-2/50 | 4.7 | % |
| elongation | Break | ASTM D638 | 96 | % |
| Tensile strain | Break | ISO 527-2/50 | 97 | % |
| Bending modulus | 50.0mmSpan | ASTM D790 | 2670 | Mpa |
| ISO 178 | 2370 | Mpa | ||
| bending strength | ISO 178 | 94.8 | Mpa | |
| Yield,50.0mmSpan | ASTM D790 | 102 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | TD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C |
| MD：-40to40°C | ISO 11359-2 | 7E-05 | cm/cm/°C | |
| MD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C | |
| RTI Str | UL 746 | 80.0 | °C | |
| Ball Pressure Test | 75°C | IEC 60695-10-2 | Pass | |
| Vicat softening temperature | -- | ISO 306/B120 | 114 | °C |
| -- | ISO 306/B50 | 113 | °C | |
| ASTM D152511 | 111 | °C | ||
| Linear coefficient of thermal expansion | TD：-40to40°C | ISO 11359-2 | 7E-05 | cm/cm/°C |
| RTI Elec | UL 746 | 80.0 | °C | |
| RTI Imp | UL 746 | 80.0 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTM D648 | 106 | °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 96.1 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.35 | % |
| Shrinkage rate | TD：3.20mm | Internal Method | 0.50-0.70 | % |
| MD：3.20mm | Internal Method | 0.50-0.70 | % | |
| MD：--2 | Internal Method | 0.50-0.70 | % | |
| Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 23.2 | cm3/10min |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 25 | g/10min |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.15 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dissipation factor | 1MHz | IEC 60250 | 0.010 | |
| 60Hz | IEC 60250 | 0.030 | ||
| 50Hz | IEC 60250 | 0.030 | ||
| Relative permittivity | 1MHz | IEC 60250 | 2.90 | |
| 60Hz | IEC 60250 | 3.00 | ||
| 50Hz | IEC 60250 | 3.00 | ||
| Dielectric strength | 1.60mm,inOil | ASTM D149 | 27 | KV/mm |
| Volume resistivity | IEC 60093 | >1.0E+15 | ohms·cm | |
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.