Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC BPL1000 BK SABIC INNOVATIVE US
LEXAN™
Automotive components、Electronic and electrical、Thin walled products
UV resistance、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/BPL1000 BK |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 18 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 48.6 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 12 kJ/m² |
| 23°C | ISO 180/1A | 18 kJ/m² |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/BPL1000 BK |
|---|---|---|---|
| relative permittivity | 60Hz | IEC 60250 | 3.00 |
| dielectric strength | 1.60mm,inOil | ASTM D149 | 27 KV/mm |
| relative permittivity | 50Hz | IEC 60250 | 3.00 |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 2.90 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Dissipation Factor | 50Hz | IEC 60250 | 0.030 |
| 60Hz | IEC 60250 | 0.030 | |
| 1MHz | IEC 60250 | 0.010 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/BPL1000 BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2460 Mpa | |
| elongation | 屈服 | ASTM D638 | 4.8 % |
| Flexural modulus | 50.0mmSpan | ASTM D790 | 2670 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.7 % |
| tensile strength | 断裂 | ISO 527-2/50 | 53.5 Mpa |
| Tensile modulus | ASTM D638 | 2680 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 64.8 Mpa |
| elongation | 断裂 | ASTM D638 | 96 % |
| tensile strength | Break | ASTM D638 | 51.0 Mpa |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 102 Mpa |
| ISO 178 | 94.8 Mpa | ||
| Flexural modulus | ISO 178 | 2370 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 63.4 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 97 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/BPL1000 BK |
|---|---|---|---|
| UL flame retardant rating | 0.45mm | UL 94 | V-2 |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 800 °C |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| Limiting Oxygen Index | ISO 4589-2 | 36 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/BPL1000 BK |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 23.2 cm3/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| Shrinkage rate | MD：--2 | 内部方法 | 0.50-0.70 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.35 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 25 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/BPL1000 BK |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 106 °C |
| vicat | ASTM D152511 | 111 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| RTI Str | UL 746 | 80.0 °C | |
| vicat | -- | ISO 306/B120 | 114 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| vicat | -- | ISO 306/B50 | 113 °C |
| RTI Imp | UL 746 | 80.0 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 96.1 °C |
| RTI Elec | UL 746 | 80.0 °C |