PPO NORYL™  GFN3-701 SABIC INNOVATIVE THAILAND

249
  • Unit Price:US$ 2,944 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    16MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:enhance｜Glass fiber reinforced｜Hydrolysis resistance
  • Application Areas:Lawn equipment｜Garden equipment｜Non specific food｜Outdoor applications｜Electrical field｜Electronic field｜Architectural application field｜Liquid handling｜Electrical appliances｜Engine hood parts｜Medical supplies｜Nursing supplies｜Plastic bag｜Automotive External Parts｜Lighting applications
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

hardnessTest ConditionTest MethodTest Result
Rockwell hardnessL-SaleASTM D785108
thermal performanceTest ConditionTest MethodTest Result
RTI ElecUL 74690.0 °C
RTI ImpUL 74690.0 °C
RTI StrUL 74690.0 °C
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648142 °C
Hot deformation temperature0.45MPa,Unannealed,6.40mmASTM D648158 °C
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf143 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648137 °C
Hot deformation temperature1.8MPa,Unannealed,6.40mmASTM D648138 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af137 °C
Vicat softening temperature--ISO 306/B50143 °C
Vicat softening temperature--ISO 306/B120147 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8313.1E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8316.2E-05 cm/cm/°C
flammabilityTest ConditionTest MethodTest Result
Extreme Oxygen IndexASTM D286326 %
UL flame retardant rating1.5mmUL 94HB
Electrical performanceTest ConditionTest MethodTest Result
Hot wire ignitionHWIUL 746PLC 4
High voltage arc tracing rateHVTRUL 746PLC 3
High arc combustion indexHAIUL 746PLC 4
Dielectric strength3.20mm,inOilASTM D14922 KV/mm
Dielectric constant50HzASTM D1502.93
Dielectric constant60HzASTM D1502.93
Dissipation factor50HzASTM D1509E-04
Dissipation factor60HzASTM D1509E-04
Arc resistanceASTM D495PLC7
Compared to the anti leakage trace indexCTIUL 746PLC 4
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rate24hrASTM D5700.060 %
Shrinkage rateMD：3.20mmInternal Method0.10-0.40 %
Melt Volume Flow Rate (MVR)300°C/5.0kgISO 11337.82 cm3/10min
melt mass-flow rate300°C/5.0kgASTM D12388.7 g/10min
mechanical propertiesTest ConditionTest MethodTest Result
tensile strengthBreakISO 527-2117 Mpa
tensile strengthBreakASTM D638116 Mpa
Tensile modulusISO 527-2/18740 Mpa
Tensile modulusASTM D6389150 Mpa
bending strengthYield,100mmSpan4ASTM D790162 Mpa
bending strengthYield,50.0mmSpan5ASTM D790180 Mpa
bending strengthISO 178183 Mpa
Bending modulusISO 1788710 Mpa
Bending modulus50.0mmSpan5ASTM D7908000 Mpa
Bending modulus100mmSpan4ASTM D7907170 Mpa
Tensile strainBreakISO 527-21.8 %
elongationBreakASTM D6382.0 %
impact performanceTest ConditionTest MethodTest Result
Impact strength of cantilever beam gap23°CISO 180/1A12 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U36 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U32 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A12 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU39 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU47 kJ/m²
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.