PMMA DELPET™ 80N ASAHI JAPAN
349
- Unit Price:US$ 2,835 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:106MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:PMMA ACRYREX® CM-205 TAIWAN CHIMEI
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:transparent｜Chemical resistance｜transparent｜Excellent surface hardness｜Weather resistance｜Chemical resistance｜heat-resisting｜High mechanical strength
- Application Areas:Casters｜Automotive Applications｜Suitable for using heat-resistant products in injection molding engineering
- Color:--
- Grade:Heat resistant grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmittance | 93 % | ||
| refractive index | 1.19 | ||
| Shrinkage rate | 0.002-0.006 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmittance | ASTM D1003/ISO 13468 | 92 % | |
| refractive index | ASTM D542/ISO 489 | 1.49 | |
| transmittance | 93 % |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 一般耐热用途 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 2.0 g/10min | ||
| Water absorption rate | 0.3 % | ||
| UL standard | 94HB | ||
| melt mass-flow rate | ASTM D1238 | 2 g/10min | |
| 0.9 g/10min | |||
| Water absorption rate | ASTM D570 | 0.3 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural modulus | 3300 Mpa | ||
| bending strength | 120 Mpa | ||
| Shrinkage rate | 0.002-0.006 cm/cm | ||
| elongation | 5 % | ||
| Impact strength of cantilever beam gap | 1.6 kJ/m² | ||
| Rockwell hardness | 100 M-scale/R-scale | ||
| tensile strength | 73 Mpa | ||
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 1.6 kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | ASTM D638/ISO 527 | 73 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 5 % | |
| Rockwell hardness | ASTM D785 | M100 | |
| Flexural modulus | ASTM D790/ISO 178 | 3300 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 120 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 6 % | |
| Impact strength of cantilever beam gap | 0.016 KJ/m | ||
| Rockwell hardness | 100 M标度 | ||
| tensile strength | 74.0 Mpa | ||
| elongation | 5 % | ||
| bending strength | 120.0 Mpa | ||
| Flexural modulus | 3400 Mpa |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.19 | |
| Shrinkage rate | ASTM D955 | 0.002-0.006 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 2 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.3 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | 6×10-5 cm/cm.℃ | ||
| Heat distortion temperature | 100 °C | ||
| ASTM D648/ISO 75 | 100 ℃（℉） | ||
| ASTM D648/ISO 75 | 109 ℃（℉） | ||
| 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.