Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PMMA 80N ASAHI JAPAN
DELPET™
Casters、Automotive Applications、Suitable for using heat-r
transparent、Chemical resistance、transparent、Excellent surface hardnes、Weather resistance、Chemical resistance、heat-resisting、High mechanical strength
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/80N |
|---|---|---|---|
| Water absorption rate | 0.3 % | ||
| UL standard | 94HB | ||
| melt mass-flow rate | 条件I | ASTM D1238 | 2 g/10min |
| Water absorption rate | ASTM D570 | 0.3 % | |
| melt mass-flow rate | 条件L | 0.9 g/10min | |
| 2.0 g/10min |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/80N |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 1.6 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 120 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 3300 kg/cm²(MPa)[Lb/in²] | |
| bending strength | 120.0 Mpa | ||
| elongation | ASTM D638/ISO 527 | 5 % | |
| Rockwell hardness | 100 M-scale/R-scale | ||
| elongation at break | ASTM D638/ISO 527 | 6 % | |
| Shrinkage rate | 0.002-0.006 cm/cm | ||
| tensile strength | 74.0 Mpa | ||
| Rockwell hardness | ASTM D785 | M100 | |
| tensile strength | ASTM D638/ISO 527 | 73 kg/cm²(MPa)[Lb/in²] | |
| elongation | 5 % | ||
| Impact strength of cantilever beam gap | 1.6 kJ/m² | ||
| 悬臂梁V型缺口 | 0.016 KJ/m | ||
| Flexural modulus | 3400 Mpa | ||
| Rockwell hardness | 100 M标度 | ||
| elongation | 断裂 | 5 % |
| optical performance | Test Condition | Test Method | ASAHI JAPAN/80N |
|---|---|---|---|
| transmittance | 93 % | ||
| refractive index | ASTM D542/ISO 489 | 1.49 | |
| transmittance | ASTM D1003/ISO 13468 | 92 % |
| other | Test Condition | Test Method | ASAHI JAPAN/80N |
|---|---|---|---|
| characteristic | 一般耐热用途 |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/80N |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.002-0.006 % | |
| density | ASTM D792/ISO 1183 | 1.19 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 2 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.3 % |
| physical property | Test Condition | Test Method | ASAHI JAPAN/80N |
|---|---|---|---|
| Shrinkage rate | 0.002-0.006 % | ||
| transmittance | 93 % | ||
| refractive index | 1.19 |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/80N |
|---|---|---|---|
| Heat distortion temperature | HDT | 100 °C | |
| HDT | ASTM D648/ISO 75 | 109 ℃（℉） | |
| 经退火，HDT | 100 °C | ||
| Linear coefficient of thermal expansion | 6×10-5 cm/cm.℃ |