Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 100 |
| processability | Test Condition | Test Method | Test Result |
|---|
| shrinkage rate | 流动方向，80℃×2mmt | ISO 11359-2 | 0.3 % |
| shrinkage rate | 垂直方向，80℃×2mmt | - | 0.7 % |
| thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | 1.8MPa | ISO 75-1 | 265 °C |
| Linear coefficient of thermal expansion | 流动方向 | ISO 11359-2 | 2 |
| Linear coefficient of thermal expansion | 垂直方向 | - | 4 |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 265 °C |
| Linear coefficient of thermal expansion | MD | 内部方法 | 2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD | 内部方法 | 4E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.69 g/cm |
| Water absorption rate | 23℃,水中24小时 | ISO 62 | 0.03 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ColorNumber | | | HD9000 |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | 310℃,1000/sec | ISO 11443 | 340 Pa·s |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| melt viscosity | 310°C,1000sec^-1 | ISO 11443 | 340000 mPa·s |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 90 Ω |
| volume resistivity | | IEC 60093 | 100 Ω·cm |
| volume resistivity | | IEC 60093 | 1E+02 ohms·cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.030 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO 527-2 | 135 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 1.5 % |
| flexural modulus | | ISO 178 | 12000 Mpa |
| bending strength | | ISO 178 | 195 Mpa |
| tensile strength | | ISO 527-1 | 135 Mpa |
| bending strength | | ISO 178 | 195 Mpa |
| fracture strain | | ISO 527-1 | 1.5 % |
| Charpy Notched Impact Strength | | ISO 179/1eA | 5.0 KJ/m |
| flexural modulus | | ISO 178 | 12000 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.