PA66/PTFE LNP™ LUBRICOMP™ RL-4020 SABIC INNOVATIVE US

503

Unit Price:US$ 6,310 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜resist fatigue
Application Areas:Electronic and electrical accessories｜Automotive components｜Casters
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	--	ISO 6603-2	4.20	J
Dart impact	Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	3.59	J
Suspended wall beam without notch impact strength	23°C3	ISO 180/1U	59	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D4812	900	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--	ISO 527-2/1	3180	Mpa
tensile strength	Yield	ASTM D638	75.1	Mpa
	tensile strength	Yield	ISO 527-2	73.0	Mpa
		tensile strength	Break	ASTM D638	74.7	Mpa
		tensile strength	tensile strength	Break	ISO 527-2	73.0	Mpa
elongation	Yield	ASTM D638	14	%
Tensile modulus	--2	ASTM D638	3090	Mpa
Wear factor	Washer	ASTM D3702Modified	49.0	10^-10in^5-min/ft-lb-hr
Friction coefficient	Static	ASTM D3702Modified	0.23
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702Modified	0.27
bending strength	--	ISO 178	89.4	Mpa
bending strength	bending strength	--	ASTM D790	112	Mpa
Bending modulus	--	ISO 178	2840	Mpa
Bending modulus	Bending modulus	--	ASTM D790	3040	Mpa
elongation	Break	ISO 527-2	18	%
	elongation	Break	ASTM D638	14	%
	elongation	elongation	Yield	ISO 527-2	17	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	8.6E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	8.3E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan4	ISO 75-2/Af	74.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	76.1	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2	%
Water absorption rate	Water absorption rate	24hr,50%RH	ASTM D570	0.94	%
Shrinkage rate	MD:24hr	ISO 294-4	2.2	%
	Shrinkage rate	TD:24hr	ISO 294-4	2.6	%
		Shrinkage rate	TD:24hr	ASTM D955	2.6	%
		Shrinkage rate	Shrinkage rate	MD:24hr	ASTM D955	2.2	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Tenamo (Guangdong)	US$ 4940 /MT

Supplier Join

Get App

Top

PA66/PTFE LNP™ LUBRICOMP™ RL-4020 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index