PA66/PTFE RL-4020 SABIC INNOVATIVE US
LNP™ LUBRICOMP™ 
Electronic and electrical、Automotive components、Casters
High temperature resistan、resist fatigue
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/RL-4020
Suspended wall beam without notch impact strength23°CASTM D4812900 J/m
23°C3ISO 180/1U59 kJ/m²
Dart impact--ISO 6603-24.20 J
23°C,EnergyatPeakLoadASTM D37633.59 J
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/RL-4020
Tensile modulus--2ASTM D6383090 Mpa
elongation屈服ASTM D63814 %
Flexural modulus--ISO 1782840 Mpa
Wear factorWasherASTM D3702Modified49.0 10^-10in^5-min/ft-lb-hr
tensile strength 断裂ASTM D63874.7 Mpa
断裂ISO 527-273.0 Mpa
bending strength--ISO 17889.4 Mpa
elongation屈服ISO 527-217 %
断裂ASTM D63814 %
bending strength--ASTM D790112 Mpa
coefficient of frictionStaticASTM D3702Modified0.23
tensile strength 屈服ASTM D63875.1 Mpa
屈服ISO 527-273.0 Mpa
coefficient of frictionDynamicASTM D3702Modified0.27
Tensile modulus--ISO 527-2/13180 Mpa
Flexural modulus--ASTM D7903040 Mpa
elongation断裂ISO 527-218 %
physical property Test ConditionTest MethodSABIC INNOVATIVE US/RL-4020
Shrinkage rateMD:24小时ISO 294-42.2 %
Water absorption rate24hr,50%RHASTM D5700.94 %
Shrinkage rateTD:24小时ASTM D9552.6 %
Water absorption rate平衡,23°C,50%RHISO 621.2 %
Shrinkage rateMD:24小时ASTM D9552.2 %
TD:24小时ISO 294-42.6 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/RL-4020
Heat distortion temperature1.8MPa,未退火,64.0mm跨距4,HDTISO 75-2/Af74.0 °C
Linear coefficient of thermal expansionTD:-40到40°CASTME8318.6E-05 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,3.20mm,HDTASTM D64876.1 °C
Linear coefficient of thermal expansionMD:-40到40°CASTME8318.3E-05 cm/cm/°C