ABS Toyolac® 920 TORAY MALAYSIA
1368
- Unit Price:US$ 2,171 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:648.6MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:high strength｜transparent
- Application Areas:Electronic field｜Automotive sector｜Electrical field｜Electric appliances
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility | UL-94 | ||
| Hot deformation temperature | 18.56kg/cm | ASTM D-648 | 89 ℃ |
| Combustibility (rate) | UL 94 | HB | |
| Hot deformation temperature | HDT | ASTM D648/ISO 75 | 89 ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.2x10^-4 mm/mm.℃ |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Color | 白黑.透明 |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt viscosity | 220℃ | ×10 | 插入式粘度计 |
| Basic Performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 浸入23℃水中24hr | ASTM D-570 | 0.3 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.08 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.3 % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 19-23 g/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 23℃，Yield | ASTM D-638 | 490 kg/cm |
| Rockwell hardness | 23℃ | ASTM D-785 | 115 R |
| bending strength | 23℃ | ASTM D-790 | 780 kg/cm |
| Elongation at Break | 23℃ | ASTM D-638 | 380 kg/cm |
| tensile strength | ASTM D638/ISO 527 | 490（屈服）380（断裂） kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 3.5 % | |
| Rockwell hardness | ASTM D785 | R-115 | |
| Bending modulus | ASTM D790/ISO 178 | 23500 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 780 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 13 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 6 kg·cm/cm(J/M)ft·lb/in | ||
| Elongation at Break | ASTM D638/ISO 527 | 30 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.