ABS 920 TORAY MALAYSIA
Toyolac®
Electronic field、Automotive sector、Electrical field、Electric appliances
high strength、transparent
RoHS
UL
MSDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | TORAY MALAYSIA/920 |
|---|---|---|---|
| melt viscosity | 220℃ | ×10 | 插入式粘度计 |
| Basic performance | Test Condition | Test Method | TORAY MALAYSIA/920 |
|---|---|---|---|
| Water absorption | 浸入23℃水中24小时 | ASTM D-570 | 0.3 % |
| Mechanical properties | Test Condition | Test Method | TORAY MALAYSIA/920 |
|---|---|---|---|
| yield strength | 23℃ | ASTM D-638 | 490 kg/cm |
| bending strength | ASTM D790/ISO 178 | 780 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 23500 kg/cm²(MPa)[Lb/in²] | |
| Izod notch impact strength | ASTM D256/ISO 179 | 6 kg·cm/cm(J/M)ft·lb/in | |
| elongation | ASTM D638/ISO 527 | 3.5 % | |
| breaking strength | 23℃ | ASTM D-638 | 380 kg/cm |
| Rockwell hardness | 23℃ | ASTM D-785 | 115 R |
| ASTM D785 | R-115 | ||
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 30 % | |
| tensile strength | ASTM D638/ISO 527 | 490（屈服）380（断裂） kg/cm²(MPa)[Lb/in²] | |
| 23℃ | ASTM D-790 | 780 kg/cm |
| other | Test Condition | Test Method | TORAY MALAYSIA/920 |
|---|---|---|---|
| colour | 白黑，透明 |
| Physical properties | Test Condition | Test Method | TORAY MALAYSIA/920 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.08 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 19~23 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.3 % |
| Thermal performance | Test Condition | Test Method | TORAY MALAYSIA/920 |
|---|---|---|---|
| combustibility | UL-94 | ||
| ASTM D648/ISO 75 | 89 ℃（℉） | ||
| Combustibility (rate) | UL94 | HB | |
| 18.56kg/cm | ASTM D-648 | 89 ℃ | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 1.2x10^-4 mm/mm.℃ |